ASA GELOY™ CR7520 GY6C348 SABIC INNOVATIVE US
125
- Unit Price:
- $2371 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High temperature resistan High mobility
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.06 | g/cm³ | |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
| 260°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| 280°C/3.8kg | ASTMD1238 | 20 | g/10min | |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Equilibrium,23°C | ASTMD570 | 0.55 | % |
| Outdoor applicability | UL746C | f2 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 1790 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2000 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 41.4 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 39.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 34.5 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 29.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 3.1 | % |
| Elongation rate 4 | Break | ASTMD638 | 40 | % |
| Tensile strain | Break | ISO527-2/50 | 44 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 1790 | Mpa |
| Bending modulus 5 | ISO178 | 2000 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 58.6 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 87.8 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 90.6 | °C | |
| Hot deformation temperature 8 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 91.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 76.7 | °C |
| Evolution Calendar intelligent importer | UL746 | 50.0 | °C | |
| RTIStr | UL746 | 50.0 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 79.4 | °C |
| Hot deformation temperature 8 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 80.0 | °C |
| Hot deformation temperature | 1.8MPa,Annealed | ASTMD648 | 95.6 | °C |
| Vicat softening temperature | ASTMD15259 | 99.4 | °C | |
| ISO306/B50 | 90.0 | °C | ||
| Linear coefficient of thermal expansion | MD：-30to0°C | ASTME831 | 8.5E-05 | cm/cm/°C |
| MD：-40to40°C | ASTME831 | 8.6E-05 | cm/cm/°C | |
| MD：0to100°C | ASTME831 | 9E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 9.2E-05 | cm/cm/°C | |
| RTIElec | UL746 | 50.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 16 | KV/mm |
| Dielectric constant | 50Hz | ASTMD150 | 5.20 | |
| 60Hz | ASTMD150 | 5.20 | ||
| 1MHz | ASTMD150 | 3.21 | ||
| Dissipation factor | 50Hz | ASTMD150 | 0.15 | |
| 60Hz | ASTMD150 | 0.15 | ||
| 1MHz | ASTMD150 | 0.026 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC3 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength6 | 23°C | ISO179/1eA | 17 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 59 | J/m |
| 23°C | ASTMD256 | 320 | J/m | |
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 4.5 | kJ/m² |
| 23°C | ISO180/1A | 19 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 20.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 35.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 86 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner glossiness | 60°,无织构 | ASTMD523 | 95 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.