ASA GELOY™ XP4034 WH9B273 SABIC INNOVATIVE US
121
- Unit Price:
- $3691 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High temperature resistan Antistatic Thermal stability Weather resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 5.0 | g/10min |
| 260°C/5.0kg | ASTMD1238 | 14 | g/10min | |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.25 | % |
| Melt mass flow rate | 280°C/3.8kg | ASTMD1238 | 24 | g/10min |
| density | ASTMD792 | 1.15 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | 屈服 | ASTMD638 | 62.1 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 57.0 | Mpa |
| 断裂 | ISO527-2/50 | 50.0 | Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 4.5 | % |
| elongation | 断裂 | ASTMD638 | 25 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 130 | % |
| Tensile modulus | ISO527-2/1 | 2500 | Mpa | |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 2520 | Mpa |
| ISO178 | 2500 | Mpa | ||
| bending strength | ISO178 | 75.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 88.3 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| thermal conductivity | ASTMC177 | 0.25 | W/m/K | |
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 104 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 98.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 113 | °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| TD：-20to150°C | ASTME831 | 7.2E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 116 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 116 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 30.5 | J |
| 23°C,TotalEnergy | ASTMD3763 | 47.5 | J | |
| Charpynotchedimimpact string | 23°C | ISO179/1eA | 32 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 80 | J/m |
| 23°C | ASTMD256 | 320 | J/m | |
| -30°C | ISO180/1A | 7.0 | kJ/m² | |
| 23°C | ISO180/1A | 33 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.