ASA GELOY™ HRA222 SABIC INNOVATIVE US
133
- Unit Price:
- $4062 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Flame retardant
- Application Areas:Electrical field Electrical appliances Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.60 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Molten Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 13.0 | cm3/10min |
| Shrinkage rate - Flow 2 | 内部方法 | 0.40 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 6 | ISO 178 | 2510 | Mpa | |
| Bending stress 6, 7 | ISO 178 | 93.0 | Mpa | |
| Tensile modulus | -- 3 | ASTM D638 | 2590 | Mpa |
| -- | ISO 527-2/1 | 2520 | Mpa | |
| elongation | Yield 5 | ASTM D638 | 4.2 | % |
| Yield 4 | ASTM D638 | 4.3 | % | |
| Yield | ISO 527-2/5 | 4.3 | % | |
| Yield | ISO 527-2/50 | 4.4 | % | |
| Break 5 | ASTM D638 | > 100 | % | |
| Break 4 | ASTM D638 | > 100 | % | |
| Break | ISO 527-2/5, ISO 527-2/50 | > 50 | % | |
| Tensile strength | Yield 4 | ASTM D638 | 63.0 | Mpa |
| Yield 5 | ASTM D638 | 59.0 | Mpa | |
| Yield | ISO 527-2/5 | 62.0 | Mpa | |
| Yield | ISO 527-2/50 | 60.0 | Mpa | |
| Break 5 | ASTM D638 | 66.0 | Mpa | |
| Break 4 | ASTM D638 | 56.0 | Mpa | |
| Break | ISO 527-2/5 | 51.0 | Mpa | |
| Break | ISO 527-2/50 | 45.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO 306/A50 | 111 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 104 | °C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -30 to 80°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C |
| Across Flow : -30 to 80°C | ISO 11359-2 | 7.1E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| Hot deformation temperature 10 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 99.0 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 88.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 230 到 270 | °C | ||
| Mold temperature | 50 到 70 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Temperature at the rear of the barrel | 200 到 230 | °C | ||
| Temperature in the middle of the barrel | 220 到 260 | °C | ||
| Temperature at the front of the material cylinder | 230 到 270 | °C | ||
| Spray nozzle temperature | 220 到 260 | °C | ||
| Hopper temperature | 60 到 80 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 29 | % | |
| UL flame retardant rating | 0.8 mm | UL 94 | V-2 | |
| 2.0 mm | UL 94 | V-0 | ||
| 2.3 mm | UL 94 | 5VB | ||
| 2.3 mm, Testing by SABIC | UL 94 | 5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.