COC Polyester OKP4HT OSAKA GAS JAPAN
192
- Unit Price:
- $14862 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.26 | ||
| Molding shrinkage rate | ASTM D955 | 0.7 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 3 | g/10min | |
| ASTM D1238/ISO 1133 | 10 | g/10min | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | 10 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 65 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 2500 | % | |
| Bending modulus | ASTM D790/ISO 178 | 65 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 115 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 43 | kg·cm/cm(J/M)ft·lb/in | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 2500 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature | ASTM D785 | 142 | ℃（℉） | |
| Hot deformation temperature | ASTM D648/ISO 75 | 128 | ℃（℉） | |
| Combustibility (rate) | UL94 | HB |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 80°-90°五小时以上 | |||
| Processing temperature | 300 | ℃（℉） | ||
| 250 | ℃（℉） | |||
| 280 | ℃（℉） | |||
| 230 | ℃（℉） | |||
| Screw speed | 20mm/s | rpm | ||
| Mold temperature | 100-120 | ℃（℉） | ||
| Melt Temperature | 280 | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 90% | |||
| Fuzzy coefficient (Haze) | ISO 14782 | 83% | % | |
| Light transmittance | ASTM D1003/ISO 13468 | 90 | % | |
| Refractive index | ASTM D542/ISO 489 | 1.632 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.