Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 367°C/6.6kg | ASTMD1238 | 31 | g/10min |
| Shrinkage rate | MD:24hr | ASTMD955 | 0.20到0.40 | % |
| Shrinkage rate | TD:24hr | ASTMD955 | 0.50到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| --2 | | ASTMD638 | 9170 | Mpa |
| Fracture 3 | | ASTMD638 | 158 | Mpa |
| crack | | ISO527-2/5 | 156 | Mpa |
| Fracture 4 | | ASTMD638 | 2.4 | % |
| crack | | ISO527-2/5 | 2.3 | % |
| 50.0mm span 5 | | ASTMD790 | 8140 | Mpa |
| --6 | | ISO178 | 8410 | Mpa |
| --7 | | ISO178 | 225 | Mpa |
| Fracture, 50.0mm span 8 | | ASTMD790 | 224 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| 1.8MPa, unannealed, 6.40mm | | ASTMD648 | 197 | °C |
| 1.8MPa, unannealed, 64.0mm span of 10 | | ISO75-2/Af | 201 | °C |
| Linear coefficient of thermal expansion | MD:40to120°C | ASTME831 | 1.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD:40to120°C | ASTME831 | 6.3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTMD257 | 4E+05 | ohms |
| Volume resistivity | | ASTMD257 | 5.1E+05 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam gap 9 | 23°C | ISO179/1eA | 3.6 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.600mm,TestingbySABIC | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.