PEI ULTEM™ 9085 WH8E479 SABIC INNOVATIVE US
128
- Unit Price:
- $24962 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 14.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Low toxicity Low smoke
- Application Areas:Aircraft interior parts national defense Railway Applications Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 295°C/6.6kg | ASTMD1238 | 8.9 | g/10min |
| Melt volume flow rate | 360°C/5.0kg | ISO1133 | 65.5 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.39 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.17 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/5 | 88.0 | Mpa |
| Break | ISO527-2/5 | 71.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 6.7 | % |
| Break | ISO527-2/5 | 50 | % | |
| Tensile modulus | ISO527-2/1 | 3050 | Mpa | |
| Bending modulus 5 | ISO178 | 2750 | Mpa | |
| Bending strength 5,6 | ISO178 | 90.0 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile modulus 2 | ASTMD638 | 3440 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 84.0 | Mpa |
| Break | ASTMD638 | 74.0 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2920 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 138 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 72 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 153 | °C |
| Vicat softening temperature | ISO306/B120 | 173 | °C | |
| Hot deformation temperature 8 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 152 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 13 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FAAFlammability9 | FAR25.853 | <5 | ||
| OSU peak heat release rate 10 | FAR25.853 | 36.0 | kW/m² | |
| OSU total heat release 11 | FAR25.853 | 16.0 | kW·min/m² | |
| VerticalBurnTest | 60s),passesat | FAR25.853 | 2.0 | sec |
| Extreme Oxygen Index | ASTMD2863 | 49 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.