PEI ULTEM™ HU2100 7H8D479 SABIC INNOVATIVE US
123
- Unit Price:
- $12464 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Biocompatibility Steam sterilization
- Application Areas:Medical and nursing suppl Medical devices
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.60 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 1.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.60 | % | |
| Melt volume flow rate | 360°C/5.0kg | ISO1133 | 9.00 | cm3/10min |
| Melt mass flow rate | 200°C/3.8kg | ASTMD1238 | 5.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 5,6 | ISO178 | 185 | Mpa | |
| Tensile modulus | ISO527-2/1 | 4500 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 6.0 | % |
| Bending modulus 5 | ISO178 | 4500 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 6.0 | % |
| Tensile modulus 2 | ASTMD638 | 4680 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 115 | Mpa |
| Yield | ASTMD638 | 114 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 5500 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 160 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 115 | Mpa |
| Break | ISO527-2/5 | 115 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 4.0 | % |
| Break | ISO527-2/5 | 4.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 170 | °C | |
| Evolution Calendar intelligent importer | UL746 | 170 | °C | |
| RTIStr | UL746 | 170 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 3.2E-05 | cm/cm/°C |
| MD：23to150°C | ISO11359-2 | 2.6E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 6E-05 | cm/cm/°C | |
| TD：23to150°C | ISO11359-2 | 6E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 205 | °C |
| Vicat softening temperature | ASTMD152510 | 223 | °C | |
| -- | ISO306/B50 | 212 | °C | |
| -- | ISO306/B120 | 217 | °C | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | IEC60112 | 150 | V | |
| Dielectric strength | 3.20mm,in Oil | IEC60243-1 | 15 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 10.0 | J |
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 7.0 | kJ/m² |
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | 30 | kJ/m² |
| 23°C | ISO180/1U | 30 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.