PEI LNP™ COLORCOMP™ EX10304C-BK1D414 SABIC INNOVATIVE US
114
- Unit Price:
- $16234 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced lubrication
- Application Areas:Electrical and Electronic Automotive components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow24hr | ASTM D955 | 0.5-0.7 | % |
| 垂直24hr | ASTM D955 | 0.5~07 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam gap impact | 23℃ | ASTM D256 | 34 | J/m |
| Cantilever beam without notch impact | 23℃ | ASTM D4812 | 1335 | J/m |
| Tensile modulus | 5mm/min | ASTM D638 | 3290 | Mpa |
| tensile strength | Yield5mm/minI型 | ASTM D638 | 106 | Mpa |
| Break5mm/min I型 | ASTM D638 | 95 | Mpa | |
| elongation | Yield5mm/min I型 | ASTM D638 | 7 | % |
| 斯裂5mm/min I型 | ASTM D638 | 60 | % | |
| Bending modulus | 1.3mm/min | ASTM D790 | 3020 | Mpa |
| Bending strength fracture | 23℃ | ASTM D790 | 160 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature without annealing | 1.8MPa 6.4mm | ASTM D648 | 200 | % |
| Fire resistance performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 0.8mm | UL94 | V2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.