PEI LNP™ THERMOCOMP™ EC008PXQ SABIC INNOVATIVE US
115
- Unit Price:
- $17122 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Low temperature resistanc
- Application Areas:Electronic and Electrical
- Color:--
- Grade:Conductive grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：24hr | ASTMD955 | 0.010to0.050 | % |
| TD：24hr | ASTMD955 | 0.10to0.50 | % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.11 | % |
| Melt mass flow rate | 380°C/6.7kg | ASTMD1238 | 15 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| compressive strength | 内部方法 | 222 | Mpa | |
| shear strength | ASTMC273 | 120 | Mpa | |
| shear modulus | ASTMC273 | 4660 | Mpa | |
| Poisson's ratio | ASTMD638 | 0.40 | ||
| Tensile modulus 2 | ASTMD638 | 38600 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 272 | Mpa |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 32600 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 247 | Mpa |
| Tensile strain | Break | ISO527-2/5 | 0.90 | % |
| Tensile modulus | ISO527-2/1 | 35500 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 1.0 | % |
| Bending modulus 5 | ISO178 | 30600 | Mpa | |
| Bending strength 5,6 | ISO178 | 364 | Mpa | |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 372 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 193 | °C |
| Linear coefficient of thermal expansion | MD：-40to150°C | ASTME831 | 2.7E-06 | cm/cm/°C |
| TD：-40to150°C | ASTME831 | 3.6E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 4.1E+03 | ohms | |
| Volume resistivity | ASTMD257 | 4.5E+02 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 7.30 | J |
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 6.9 | kJ/m² |
| UnnotchedIzodImpactStrength7 | 23°C | ISO180/1U | 34 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTMD785 | 112 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.