PEI ULTEM™ HU1000 2H4D342 SABIC INNOVATIVE US
149
- Unit Price:
- $11115 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Biocompatibility Steam sterilization
- Application Areas:Medical and nursing suppl Medical devices
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.25 | % |
| Saturation,23°C | ISO62 | 1.3 | % | |
| Equilibrium,23°C | ASTMD570 | 1.3 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.70 | % | |
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 9.0 | g/10min |
| Melt volume flow rate | 220°C/5.0kg | ISO1133 | 13.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 5 | ISO178 | 3300 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile modulus 2 | ASTMD638 | 3580 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 90.0 | Mpa |
| Yield | ASTMD638 | 110 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 3440 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 173 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 60 | % |
| Tensile stress | Yield | ISO527-2/5 | 105 | Mpa |
| Break | ISO527-2/5 | 85.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 6.0 | % |
| Break | ISO527-2/5 | 60 | % | |
| Tensile modulus | ISO527-2/1 | 3200 | Mpa | |
| Bending strength 5,6 | ISO178 | 160 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 201 | °C |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 5.6E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD：-20to150°C | ASTME831 | 5.4E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 215 | °C |
| Vicat softening temperature | ASTMD152510 | 219 | °C | |
| -- | ISO306/B50 | 215 | °C | |
| -- | ISO306/B120 | 211 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| Dielectric strength | 1.60mm,inAir | ASTMD149 | 33 | KV/mm |
| 1.60mm,in Oil | ASTMD149 | 28 | KV/mm | |
| Dielectric constant | 1kHz | ASTMD150 | 3.15 | |
| Volume resistivity | ASTMD257 | 1E+17 | ohms·cm | |
| Dissipation factor | 1kHz | ASTMD150 | 1.3E-03 | |
| 2.45GHz | ASTMD150 | 2.5E-03 | ||
| Arc resistance 11 | ASTMD495 | PLC5 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 4.0 | kJ/m² |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 6.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 0.700 | ||
| Extreme Oxygen Index | ASTMD2863 | 47 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.