Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.87to0.92 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.76 | % |
| Melt mass flow rate | 295°C/6.6kg | ASTMD1238 | 7.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 50.0 | mg |
| Elongation rate 4 | Break | ASTMD638 | 20 | % |
| Elongation rate 3 | Yield | ASTMD638 | 5.0 | % |
| Tensile modulus 2 | | ASTMD638 | 2400 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 53.0 | Mpa |
| Tensile strength 3 | Yield | ASTMD638 | 62.0 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 94.0 | Mpa |
| Bending modulus 5 | | ISO178 | 2000 | Mpa |
| Bending strength 5,6 | | ISO178 | 98.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 68.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 59.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 5.0 | % |
| Tensile strain | Break | ISO527-2/50 | 15 | % |
| Tensile modulus | | ISO527-2/1 | 2300 | Mpa |
| Bending modulus | -- | ASTMD790 | 2150 | Mpa |
| Bending modulus | 50.0mmSpan4 | ASTMD790 | 2150 | Mpa |
| bending strength | | ASTMD790 | 94.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 145 | °C |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 164 | °C |
| Vicat softening temperature | | ISO306/B120 | 180 | °C |
| Glass transition temperature | | DSC | 200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTMD257 | >1.0E+15 | ohms |
| Dielectric constant | 100Hz | ASTMD150 | 3.13 | |
| Dielectric constant | 100kHz | ASTMD150 | 3.07 | |
| Dielectric constant | 1MHz | ASTMD150 | 3.04 | |
| Volume resistivity | | ASTMD257 | >1.0E+16 | ohms·cm |
| Dissipation factor | 1MHz | ASTMD150 | 5.4E-03 | |
| Dissipation factor | 100Hz | ASTMD150 | 0.011 | |
| Dissipation factor | 100kHz | ASTMD150 | 6.1E-03 | |
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|
| TearStrength7 | 1.60mm | ISO34-1 | 37 | kN/m |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 8.0 | kJ/m² |
| Suspended wall beam gap impact strength 8 | 23°C | ISO180/1A | 16 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | Shore D | ASTMD2240 | 80 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ASTMD2863 | 48 | % |
| UL flame retardant rating | 1.6mm,TestingbySABIC | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.