PEI ULTEM™ 1010 WH SABIC INNOVATIVE US
155
Unit Price:$23007 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan transparent enhance Flame retardant
- Application Areas:Food service sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.25 | % |
| Equilibrium, 23°C | ASTM D570 | 1.3 | % | |
| Melt flow rate | 337°C/6.6 kg | ASTM D1238 | 18 | g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 3580 | Mpa | |
| Elongation rate 3 | Yield | ASTM D638 | 7.0 | % |
| Break | ASTM D638 | 60 | % | |
| Bending modulus | 100 mm Span | ASTM D790 | 3510 | Mpa |
| bending strength | Yield, 100 mm Span | ASTM D790 | 165 | Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 10.0 | mg |
| Tensile strength | Yield | ASTM D638 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTM D15255 | 218 | °C | |
| thermal conductivity | ASTM C177 | 0.22 | W/m/K | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C | |
| Linear coefficient of thermal expansion - flow | -20 to 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 207 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 198 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | ||
| High arc combustion index (HAI) 7 | UL 746 | PLC 3 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 | ||
| Dielectric constant | 1 kHz | ASTM D150 | 3.15 | |
| Volume resistivity | ASTM D257 | 1.0E+17 | ohms·cm | |
| Dissipation factor | 1 kHz | ASTM D150 | 1.3E-3 | |
| 2.45 GHz | ASTM D150 | 2.5E-3 | ||
| Dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Arc resistance 6 | ASTM D495 | PLC 5 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 350 到 400 | °C | ||
| Mold temperature | 135 到 165 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 330 到 400 | °C | ||
| Temperature in the middle of the barrel | 340 到 400 | °C | ||
| Temperature at the front of the material cylinder | 345 到 400 | °C | ||
| Spray nozzle temperature | 345 到 400 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Reverse notch impact | 3.20 mm | ASTM D256 | 1200 | J/m |
| Falling hammer impact | 23°C | ASTM D3029 | 33.0 | J |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1300 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 109 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTM D2863 | 44 | % | |
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.