PEI ULTEM™ HU1110 SABIC INNOVATIVE US
144
Unit Price:$10873 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Biocompatibility Steam sterilization
- Application Areas:Medical and nursing suppl Medical devices
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 16 | g/10min |
| Melt volume flow rate | 360°C/5.0kg | ISO1133 | 21.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 1.2 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.65 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 3720 | Mpa | |
| Tensile modulus | ISO527-2/1 | 3500 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 110 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 110 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 85.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile strain | Yield | ISO527-2/5 | 6.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 70 | % |
| Tensile strain | Break | ISO527-2/5 | 60 | % |
| Bending modulus | 100mmSpan4 | ASTMD790 | 3720 | Mpa |
| 50.0mmSpan5 | ASTMD790 | 3420 | Mpa | |
| Bending modulus 6 | ISO178 | 3300 | Mpa | |
| Bending strength 6,7 | ISO178 | 140 | Mpa | |
| bending strength | Yield,50.0mmSpan5 | ASTMD790 | 174 | Mpa |
| Yield,100mmSpan4 | ASTMD790 | 165 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 199 | °C |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 210 | °C |
| Vicat softening temperature | ASTMD152511 | 219 | °C | |
| -- | ISO306/B50 | 200 | °C | |
| -- | ISO306/B120 | 205 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 5.5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 5.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 5.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 5.5E-05 | cm/cm/°C | |
| RTIElec | UL746 | 170 | °C | |
| Evolution Calendar intelligent importer | UL746 | 170 | °C | |
| RTIStr | UL746 | 170 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance 12 | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Hot wire ignition | HWI | UL746 | PLC1 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpact Strength8 | 23°C | ISO179/1eA | 5.0 | kJ/m² |
| Suspended wall beam gap impact strength 9 | -30°C | ISO180/1A | 4.0 | kJ/m² |
| 23°C | ISO180/1A | 4.0 | kJ/m² | |
| ReverseNotchIzodImpact | 3.20mm | ASTMD256 | 1900 | J/m |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 28.0 | J |
| Falling hammer impact | 23°C | ASTMD3029 | 23.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71mm | UL94 | V-2 | |
| 0.75mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.