EVA TAISOX® 7140F FPC TAIWAN
125
- Unit Price:
- $3136 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:packing film currency Sanitary products
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD1505 | 0.934 | g/cm³ | |
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 0.70 | g/10min |
| Vinyl acetate content | 14.0 | wt% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield | ASTMD638 | 6.86 | Mpa |
| Break | ASTMD638 | 19.6 | Mpa | |
| elongation | Break | ASTMD638 | 750 | % |
| Bending modulus | ASTMD790 | 22.6 | Mpa | |
| friction coefficient | Blown Film | ASTMD1894 | 0.50 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittle temperature | ASTMD746 | -70.0 | °C | |
| Vicat softening temperature | ASTMD1525 | 75.0 | °C | |
| Melting temperature | 90.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 50 | µm | ||
| Available film thickness | 1.2-5.9mil(30-150µ | |||
| Secant modulus | 1%Secant,MD:50μm,Blown Film | ASTMD882 | 36.3 | Mpa |
| 1%Secant,TD:50μm,Blown Film | ASTMD882 | 41.2 | Mpa | |
| Tensile strength | MD:Yield,50μm,Blown Film | ASTMD882 | 4.90 | Mpa |
| TD:Yield,50μm,Blown Film | ASTMD882 | 3.92 | Mpa | |
| MD:Break,50μm,Blown Film | ASTMD882 | 30.4 | Mpa | |
| TD:Break,50μm,Blown Film | ASTMD882 | 27.5 | Mpa | |
| elongation | MD:Break,50μm,Blown Film | ASTMD882 | 450 | % |
| TD:Break,50μm,Blown Film | ASTMD882 | 600 | % | |
| Falling hammer impact | 50μm,Blown Film | ASTMD1709 | 620 | g |
| Elmondov tear strength | MD:50μm,Blown Film | ASTMD1922 | 20 | g |
| TD:50μm,Blown Film | ASTMD1922 | 48 | g |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore A | ASTMD2240 | 9240 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45°,50.0μm,Blown Film | ASTMD2457 | 90 | |
| Haze | 50.0μm,Blown Film | ASTMD1003 | 3.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.