PET Rynite® 545 NC010 DUPONT USA
260
Unit Price:$3432 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 157.4MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced High temperature resistan Short fiber reinforcement
- Application Areas:Fiber grade
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1690 | ||
| Molding shrinkage rate | ASTM D955 | 0.85 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.14 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.62 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.14 | % | |
| Shrinkage rate | TD | ISO294-4 | 0.80 | % |
| MD | ISO294-4 | 0.20 | % | |
| Top out temperature | 170 | °C | ||
| Melt volume flow rate | 280°C/2.16kg | ISO1133 | 2.50 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 15600 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 13300 | Mpa |
| Tensile stress | Break | ISO527-2 | 182 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.0 | % |
| Tensile modulus | ISO527-2 | 15500 | Mpa | |
| ASTM D412/ISO 527 | 15500 | kg/cm²(MPa)[Lb/in²] | ||
| Rockwell hardness | ASTM D785 | 100 | ||
| Bending modulus | ASTM D790/ISO 178 | 13500 | kg/cm²(MPa)[Lb/in²] | |
| ISO178 | 13500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 250 | ℃（℉） | |
| ASTM D648/ISO 75 | 226 | ℃（℉） | ||
| 1.8MPa,Unannealed | ISO75-2/A | 226 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 180 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 8.3E-05 | cm/cm/°C | |
| Vicat softening temperature | ISO306/B50 | 230 | °C | |
| Melting temperature 2 | ISO11357-3 | 252 | °C | |
| thermal conductivity | 0.32 | W/m/K | ||
| EffectiveThermalDiffusivity | 1.4E-07 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Dielectric strength | IEC60243-1 | 32 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.50 | |
| 1MHz | IEC60250 | 4.40 | ||
| Leakage Trace Index | IEC60112 | 250 | V | |
| Dissipation factor | 100Hz | IEC60250 | 7E-03 | |
| 1MHz | IEC60250 | 0.011 | ||
| Surface resistivity | ASTM D257/IEC 60093 | 1.00E+14 | Ω | |
| IEC60093 | 1E+14 | ohms | ||
| Dielectric constant | ASTM D150/IEC 60250 | 4.5 | ||
| ASTM D150/IEC 60250 | 4.4 | |||
| Volume resistivity | ASTM D257/IEC 60093 | 1.00E+13 | Ω.cm | |
| IEC60093 | 1E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 100 | |
| R-Sale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 20 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.