PET Rynite® 415HP-NC010 DUPONT JAPAN
138
- Unit Price:
- $2502 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 19MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Electrical tools Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.80 | % |
| TD3 | ISO294-4 | 1.2 | % | |
| MD | ISO294-4 | 0.30 | % | |
| MD3 | ISO294-4 | 0.50 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 2.5 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.25 | % | |
| Melt volume flow rate | 280°C/2.16kg | ISO1133 | 4.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strain | Break | ISO527-2 | 5.0 | % |
| Bending modulus | ISO178 | 3550 | Mpa | |
| Tensile modulus | ISO527-2 | 4700 | Mpa | |
| Tensile stress | Break | ISO527-2 | 79.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ISO306/B50 | 205 | °C | |
| Melting temperature 4 | ISO11357-3 | 250 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2E-05 | cm/cm/°C |
| MD:-40to23°C | ISO11359-2 | 9.8E-05 | cm/cm/°C | |
| MD:55to160°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD:-40to-23°C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| TD:55to160°C | ISO11359-2 | 3.2E-05 | cm/cm/°C | |
| EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 | m²/s | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 235 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 207 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+13 | ohms·cm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Leakage Trace Index | IEC60112 | 350 | V | |
| Surface resistivity | IEC60093 | 1E+13 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 25 | kJ/m² |
| 23°C | ISO179/1eU | 55 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 58 | |
| R-Sale | ISO2039-2 | 111 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 5 | 1.00mm | ISO3795 | <100 | mm/min |
| UL flame retardant rating | 0.75mm | UL94,IEC60695-11-10,-20 | HB | |
| 1.5mm | UL94,IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.