TPE Hytrel® 5526 DUPONT USA
50
- Unit Price:
- $8937 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Weather resistance UV resistance High mobility Thermal stability
- Application Areas:Electrical tools Electrical field Electrical appliances Electronic field Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % |
| Density/specific gravity | ISO1183 | 1.19 | g/cm³ | |
| Melt mass flow rate | ISO1133 | 18 | g/10min | |
| Melt volume flow rate | 220°C/2.16kg | ISO1133 | 17.5 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.4 | % |
| MD | ISO294-4 | 1.4 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.60 | % | |
| MediumDensity | 1.04 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2110 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.19 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 170 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 130 | Mpa |
| Bending modulus | ISO178 | 200 | Mpa | |
| abrasion resistance | ISO4649 | 120 | mm³ | |
| Tensile modulus | ISO527-2 | 190 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 15.0 | Mpa |
| Break | ISO527-2 | 40.0 | Mpa | |
| 5.0%Strain | ISO527-2 | 6.90 | Mpa | |
| 10%Strain | ISO527-2 | 11.0 | Mpa | |
| 50%Strain | ISO527-2 | 14.0 | Mpa | |
| Tensile strain | Yield | ISO527-2 | 35 | % |
| Break | ISO527-2 | >300 | % | |
| Nominal tensile fracture strain | ISO527-2 | 780 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 65.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Brittle temperature | ISO974 | -98.0 | °C | |
| Glass transition temperature 2 | ISO11357-2 | -20.0 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 180 | °C |
| -- | ISO306/B50 | 75.0 | °C | |
| Melting temperature 2 | ISO11357-3 | 203 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 2E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 1.8E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 2E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1.7E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 4E+13 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 20 | KV/mm | |
| Leakage Trace Index | IEC60112 | 600 | V | |
| Dissipation factor | 1MHz | IEC60250 | 0.038 | |
| 100Hz | IEC60250 | 9E-03 | ||
| Relative permittivity | 1MHz | IEC60250 | 4.60 | |
| 100Hz | IEC60250 | 4.90 |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | Across Flow | ISO34-1 | 130 | kN/m |
| 流量 | ISO34-1 | 130 | kN/m |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 30 | kJ/m² |
| -30°C,Partial Break | ISO179/1eA | 150 | kJ/m² | |
| 23°C | ISO179/1eA | NoBreak | ||
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Tensile impact strength | 23°C | ISO8256/1 | 270 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ISO868 | 55 | |
| Shore D,15sec | ISO868 | 51 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS flammability | FMVSS302 | SE/B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | UL94 | HB | ||
| 1.5mm | UL94 | HB | ||
| Burning rate 3 | 1.00mm | ISO3795 | 28 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Odor | VDA270 | 5.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.