PA12 LNP™ STAT-KON™ SX90398 SABIC INNOVATIVE US
115
- Unit Price:
- $7799 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:lubrication wear resistant Filler: proprietary fille
- Application Areas:Electrical appliances Electronic display
- Color:--
- Grade:Conductive grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.20 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.30 | % | |
| Shrinkage rate | MD：24hr | ASTMD955 | 1.1 | % |
| TD：24hr | ASTMD955 | 1.7 | % | |
| TD:24hr | ISO294-4 | 1.7 | % | |
| MD:24hr | ISO294-4 | 1.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 1910 | Mpa | |
| Tensile modulus | ISO527-2/1 | 1440 | Mpa | |
| Tensile strength | Yield | ASTMD638 | 44.0 | Mpa |
| Tensile stress | Yield | ISO527-2 | 38.0 | Mpa |
| Tensile strength | Break | ASTMD638 | 36.1 | Mpa |
| Tensile stress | Break | ISO527-2 | 35.0 | Mpa |
| elongation | Yield | ASTMD638 | 5.3 | % |
| Break | ASTMD638 | 120 | % | |
| Bending modulus | ASTMD790 | 1780 | Mpa | |
| ISO178 | 1760 | Mpa | ||
| bending strength | ASTMD790 | 62.4 | Mpa | |
| Bending stress | ISO178 | 50.9 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 114 | °C |
| Hot deformation temperature 4 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 104 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 67.7 | °C |
| Hot deformation temperature 4 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 73.8 | °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 9.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 9.9E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1.0E+2to1.0E+6 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 7.6 | kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 85 | kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 9.73 | J |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 20.8 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.