PA12 TROGAMID® CX9710 EVONIK GERMANY
210
- Unit Price:
- $9421 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 81.7MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc Scratch resistant Medium viscosity
- Application Areas:Industrial accessories Automotive Applications
- Color:--
- Grade:Transparent level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Stickiness number | ISO 307 | > 150 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D Shore D | ISO 868 | 81 | |
| Ball pressure hardness | ISO 2039-1 | 110 | Mpa | |
| Tensile modulus | 23℃ 23°C | 1400 | Mpa | |
| 80℃ 80°C | 1270 | Mpa | ||
| Tensile strength | Yield，23℃ Yield, 73°F | 60 | Mpa | |
| Yield，80℃ Yield, 176°F | 48 | Mpa | ||
| Tensile strain | Yield，23℃ Yield, 73°F | 8 | % | |
| Yield，80℃ Yield, 176°F | 5.5 | % | ||
| Nominal tensile fracture strain | 23℃ 23°C | > 50 | % | |
| 80℃ 80°C | > 50 | % | ||
| Tensile creep modulus | 1 hr 1 hr | 1400 | Mpa | |
| 1000 hr 1000 hr | 700 | Mpa | ||
| Bending modulus | ISO 178 | 1700 | Mpa | |
| bending strength | -- -- | 90 | Mpa | |
| 3.50% Strain 3.5% Strain | 50 | Mpa | ||
| Outer Fiber Strain（at maximum stress） | ISO 178 | 9 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 10000000000000 | ohms | |
| Volume resistivity | IEC 60093 | 10000000000000000 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 27 | KV/mm | |
| Relative permittivity | 23℃，100 Hz 23°C, 100 Hz | 3.6 | ||
| 23℃，1 MHz 23°C, 1 MHz | 3.2 | |||
| Dissipation factor | 23℃，100 Hz 23°C, 100 Hz | 0.012 | ||
| 23℃，1 MHz 23°C, 1 MHz | 0.033 | |||
| Compared to the leakage trace index | CTI -- 6 6 | 575 | V | |
| Solution A Solution A | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30℃ -30°C | 无断裂 | ||
| 0℃ 0°C | 无断裂 | |||
| 23℃ 23°C | 无断裂 |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | 0.80 mm 0.8 mm | HB | ||
| 1.60 mm 1.6 mm | HB | |||
| Flammability index of heating wire | 1.0 mm 1.0 mm | IEC 60695-2-12 | 800 | °C |
| Ignition temperature of heating wire | 1 mm 1.0 mm | IEC 60695-2-13 | 775 | °C |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa，Unannealed 66 psi, Unannealed | ISO 75-2/B | 122 | °C |
| 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 108 | °C | |
| Glass transition temperature | ISO 11357-2 | 140 | °C | |
| Vicat softening temperature | -- -- | ISO 306/A | 135 | °C |
| -- -- | ISO 306/B | 130 | °C | |
| Melting temperature | DSC DSC 4 | DSC | 250 | °C |
| Linear coefficient of thermal expansion CLTE | MD：23~55℃ Flow : 73 to 131°F | 0.000090 | 1/℃ | |
| TD：23~55℃ Transverse : 73 to 131°F | 0.000090 | 1/℃ | ||
| Temperature index | IEC 216 | 100 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.