PBT VALOX™ 420SEOM-1001 SABIC INNOVATIVE JAPAN

220

Unit Price:$2062 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 200MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced dimensional stability High rigidity high strength heat-resisting
Application Areas:Lawn equipment Garden equipment Industrial applications Automotive External Parts Electrical field Electronic field Architectural application Outdoor applications Electrical appliances Engine hood parts Medical supplies Nursing supplies Plastic bag Automotive interior parts Casters Household goods Petroleum Applications Natural gas supplies sporting goods Textile application Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow 2	内部方法	0.10 到 0.50	%
	Shrinkage rate	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
		Shrinkage rate	Across Flow 2	内部方法	0.40 到 0.80	%
		Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.50 到 1.0	%
Water absorption rate	Saturation, 23°C	ISO 62	0.090	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.070	%
Specific volume		ASTM D792	0.610	cm³/g
Outdoor applicability		UL 746C	f2
Melt flow rate	250°C/5.0 kg	ASTM D1238	42	g/10 min
Molten Volume Flow Rate (MVR)	250°C/5.0 kg	ISO 1133	29.0	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap	-30°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of simply supported beam gap	Impact strength of simply supported beam gap	23°C	ISO 179/1eA	7.0	kJ/m²
The impact strength of a simply supported beam without a notch is	-30°C	ISO 179/1eU	50	kJ/m²
	The impact strength of a simply supported beam without a notch is	23°C	ISO 179/1eU	50	kJ/m²
Bending stress	--	ISO 178	180	Mpa
Bending stress	Bending stress	Break, 50.0 mm Span 5	ASTM D790	186	Mpa
Ball pressure hardness	H 358/30	ISO 2039-1	118	Mpa
Tensile strength	Yield 4	ASTM D638	120	Mpa
	Tensile strength	Yield	ISO 527-2/5	120	Mpa
		Tensile strength	Break 4	ASTM D638	120	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/5	120	Mpa
Tensile modulus	-- 3	ASTM D638	12000	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	10000	Mpa
elongation	Yield 4	ASTM D638	2.0	%
	elongation	Yield	ISO 527-2/5	1.9	%
		elongation	Break 4	ASTM D638	2.0	%
		elongation	elongation	Break	ISO 527-2/5	1.9	%
Rockwell hardness	R-Scale	ASTM D785	119
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	119
Bending modulus	50.0 mm Span 5	ASTM D790	9800	Mpa
Bending modulus	Bending modulus	-- 6	ISO 178	9500	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	22.0	mg
Non notched cantilever beam impact	23°C	ASTM D4812	620	J/m
	Non notched cantilever beam impact	-30°C 8	ISO 180/1U	45	kJ/m²
	Non notched cantilever beam impact	Non notched cantilever beam impact	23°C 8	ISO 180/1U	45	kJ/m²
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	5.00	J

Thermal performance	Test Condition	Test Method	Test Result	Unit
thermal conductivity		ISO 8302	0.25	W/m/K
Vicat softening temperature	--	ASTM D152510, ISO 306/B50, ISO 306/B120	200	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	220	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	2.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	2.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.9E-5	cm/cm/°C
			Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.9E-5	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	1.2E-4	cm/cm/°C
RTI		UL 746	140	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	212	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	220	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	200	°C
			Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	195	°C
			Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	200	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	1.60 mm, in Oil	ASTM D149	24	KV/mm
	Dielectric strength	3.20 mm, in Air	ASTM D149	19	KV/mm
		Dielectric strength	0.800 mm, in Oil	IEC 60243-1	23	KV/mm
			Dielectric strength	1.60 mm, in Oil	IEC 60243-1	22	KV/mm
			Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Dissipation factor	100 Hz	ASTM D150, IEC 60250	2.0E-3
	Dissipation factor	1 MHz	ASTM D150	0.020
		Dissipation factor	50 Hz	IEC 60250	1.0E-3
			Dissipation factor	60 Hz	IEC 60250	1.0E-3
			Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.010
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Dielectric constant	100 Hz	ASTM D150, IEC 60250	3.80
	Dielectric constant	1 MHz	ASTM D150	3.70
		Dielectric constant	50 Hz	IEC 60250	3.30
			Dielectric constant	60 Hz	IEC 60250	3.30
			Dielectric constant	Dielectric constant	1 MHz	IEC 60250	3.30
Volume resistivity		ASTM D257, IEC 60093	> 1.0E+15	ohms·cm
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 4
High arc combustion index (HAI)		UL 746	PLC 0
Arc resistance		ASTM D495	PLC 6
Leakage Trace Index	--	IEC 60112	175	V
Leakage Trace Index	Leakage Trace Index	Solution B	IEC 60112	125	V
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 3
Hot wire ignition (HWI)		UL 746	PLC 2

injection	Test Result	Unit
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	255 到 275	°C
Mold temperature	65 到 90	°C
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 80	%
Temperature at the rear of the barrel	245 到 265	°C
Temperature in the middle of the barrel	250 到 270	°C
Temperature at the front of the material cylinder	255 到 275	°C
Spray nozzle temperature	250 到 270	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	50 到 80	rpm
Exhaust hole depth	0.025 到 0.038	mm

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	32	%
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.71 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.