PBT Cristin® HR5315 DUPONT USA
115
- Unit Price:
- $3381 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 37.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance Glass fiber reinforced Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Electronic and electrical
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MediumDensity | 1.14 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1860 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K | ||
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.50 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| Stickiness number | ISO307 | 95.0 | cm³/g | |
| FlowLength2 | 2.00mm | 430 | mm | |
| Shrinkage rate | -，Across Flow | % | ISO 294-4 | 1.1 |
| -，Flow | % | ISO 294-4 | 0.5 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| bending strength | 23℃ | MPa | ISO 178 | 140 |
| Non notched impact strength | -，-40 ℃, Type 1 | kJ/m² | ISO 180 | |
| -，23 ℃, Type 1 | kJ/m² | ISO 180 | 45 | |
| Gap impact strength | -，-40 ℃, Type 1, Notch A | kJ/m² | ISO 180 | |
| -，23 ℃, Type 1, Notch A | kJ/m² | ISO 180 | ||
| Tensile modulus | ISO527-2 | 5200 | Mpa | |
| Tensile stress | Break | ISO527-2 | 95.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.0 | % |
| TensileCreepModule | 1hr | ISO899-1 | 5000 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 4200 | Mpa |
| Bending modulus | ISO178 | 4700 | Mpa | |
| Bending stress | ISO178 | 150 | Mpa | |
| Fracture point tensile stress | 23℃ | MPa | ISO 527-1, -2 | |
| Fracture point tensile strain | 23℃ | % | ISO 527-1, -2 | 3 |
| Tensile modulus | 23℃ | MPa | ISO 527-1, -2 | 5200 |
| Bending modulus | 23℃ | MPa | ISO 178 | 4500 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature 3 | ISO11357-2 | 65.0 | °C | |
| Melting temperature 5 | ISO11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4.1E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Hot deformation temperature | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | |
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | ||
| 0.45MPa,Unannealed | ISO75-2/B | 220 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 42 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| 1MHz | IEC60250 | 3.60 | ||
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.010 | ||
| Leakage Trace Index | IEC60112 | 350 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 60 | kJ/m² |
| Unscented Izod impact strength | -40°C | ISO180/1U | 30 | kJ/m² |
| -30°C | ISO180/1U | 40 | kJ/m² | |
| 23°C | ISO180/1U | 45 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 30 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 115 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 4 | 1.00mm | ISO3795 | <100 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
| Extreme Oxygen Index | ISO4589-2 | 20 | % | |
| FMVSS flammability | FMVSS302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.