PBT Zytel® SK601 NC010 DUPONT SHENZHEN
119
- Unit Price:
- $2850 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf Good strength (glass fibe 20% by weight ratio) 20% filler by weight Good strength (glass fibe 20% by weight ratio) 20% filler by weight
- Application Areas:Electronic and electrical Industrial applications Automotive Applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | -，23C/59RH | % | ISO 62 | 0.15 |
| -，Sat/23C | % | ISO 62 | ||
| Shrinkage rate | -，Across Flow | % | ISO 294-4 | 1.0 |
| -，Flow | % | ISO 294-4 | ||
| Density/specific gravity | g/cm | ISO 1183 | 1.45 | |
| MediumDensity | 1.26 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1860 | J/kg/°C | ||
| Density/specific gravity | ISO1183 | 1.45 | g/cm³ | |
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| ThermalConductivityofMelt | 0.25 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 7000 | Mpa | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.2 | % |
| TensileCreepModule | 1hr | ISO899-1 | 7200 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 5600 | Mpa |
| -，1h | MPa | ISO 899-1 | 7200 | |
| -，1000h | MPa | ISO 899-1 | ||
| Charpy non notched impact strength | -，-30℃, Type 1, Edgewise | KJ/m | ISO 179 | 54 |
| -，23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 56 | |
| Charpy notch impact strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 9.8 |
| Bending modulus | ISO178 | 6500 | Mpa | |
| Bending stress | ISO178 | 180 | Mpa | |
| Charpy notch impact strength | -，23℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 7.5 |
| Fracture point tensile stress | 23℃ | MPa | ISO 527-1, -2 | |
| Fracture point tensile strain | 23℃ | % | ISO 527-1, -2 | 3.2 |
| Tensile modulus | 23℃ | MPa | ISO 527-1, -2 | 7400 |
| Bending modulus | 23℃ | MPa | ISO 178 | 6200 |
| bending strength | 23℃ | MPa | ISO 178 | 180 |
| Non notched impact strength | 23 ℃, Type 1 | KJ/m | ISO 180 | 44 |
| Gap impact strength | 23 ℃, Type 1, Notch A | KJ/m | ISO 180 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | 平行Flow ，23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | |
| 垂直Flow ，23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.000040 | |
| Hot deformation temperature | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | |
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 204 | |
| Flame retardant grade | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 204 | °C | |
| Vicat softening temperature | ISO306/B50 | 210 | °C | |
| Melting temperature 2 | ISO11357-3 | 224 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 29 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.60 | ||
| Dissipation factor | 100Hz | IEC60250 | 1.2E-03 | |
| 1MHz | IEC60250 | 0.019 | ||
| Leakage Trace Index | IEC60112 | 350 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 8.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 55 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 9.0 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 60 | kJ/m² |
| 23°C | ISO180/1U | 60 | kJ/m² |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | % | ISO 4589-1, -2 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 28 | mm/min |
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate)4 | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.