PBT CELANEX® 2500 CELANESE USA
143
- Unit Price:
- $3967 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High toughness Hydrolysis resistance Thermal stability Weather resistance UV resistance
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 40.0 | cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 1.8到2.0 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
| Melt mass flow rate | ASTMD1238 | 12 | g/10min | |
| Shrinkage rate | MD | ASTMD955 | 1.7to2.2 | % |
| TD | ISO294-4 | 1.7to2.2 | % | |
| MD | ISO294-4 | 1.7to2.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 1450 | Mpa | |
| Tensile strength | Yield,23°C | ASTMD638 | 33.8 | Mpa |
| Tensile stress | Yield | ISO527-2/1A/50 | 35.0 | Mpa |
| Tensile strain | Yield | ISO527-2/1A/50 | 5.0 | % |
| elongation | Break,23°C | ASTMD638 | 100 | % |
| Nominal tensile fracture strain | ISO527-2/1A/50 | >50 | % | |
| Bending modulus | 23°C | ISO178 | 1500 | Mpa |
| Bending stress | 23°C | ISO178 | 50.0 | Mpa |
| Tensile modulus | ISO527-2/1A/1 | 2700 | Mpa | |
| Tensile stress | Yield | ISO527-2/1A/50 | 60.0 | Mpa |
| Break | ISO527-2/1A/50 | 60.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/1A/50 | 4.0 | % |
| Nominal tensile fracture strain | ISO527-2/1A/50 | 15 | % | |
| Tensile creep modulus | 1hr | ISO899-1 | 2400 | Mpa |
| 1000hr | ISO899-1 | 1600 | Mpa | |
| Bending stress | 23°C | ISO178 | 90.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 60.0 | °C |
| Vicat softening temperature | ISO306/B50 | 190 | °C | |
| Melting temperature 3 | ISO11357-3 | 225 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 125 | °C |
| 0.45MPa,Annealed | ASTMD648 | 127 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 51.7 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 50.0 | °C | |
| Glass transition temperature 2 | ISO11357-2 | 70.0 | °C | |
| Peak melting temperature | ASTMD3418 | 225 | °C | |
| Melting temperature 2 | ISO11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 23 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Dissipation factor | 100Hz | IEC60250 | 1.3E-03 | |
| 1MHz | IEC60250 | 0.020 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density of Melt | 内部方法 | 1.110 | g/cm³ | |
| SpecificHeatCapacity of Melt | 内部方法 | 1920 | J/kg/°C | |
| ThermalConductivityofMelt | 内部方法 | 0.13 | W/m/K |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 130 | kJ/m² |
| 23°C | ISO179/1eU | 140 | kJ/m² | |
| -30°C | ISO179/1eU | 170 | kJ/m² | |
| 23°C | ISO179/1eU | 200 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 104 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB | ||
| 1.0mm | UL94 | HB | ||
| 1.5mm | UL94 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 22 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.