PBT Ultradur® B4300G3 BASF MALAYSIA
103
- Unit Price:
- $5006 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Glass fiber reinforced
- Application Areas:electrical machinery Engineering accessories Shell printed circuit board
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ISO 1183 | 1.42 | g/cm³ | |
| Melt volume flow rate | 250℃，2.16 kg 250℃/2.16 kg | ISO 1133 | 15 | cm3/10min |
| Water absorption rate | Saturation，23℃ Saturation, 73°F | ISO 62 | 0.4 | % |
| Equilibrium，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 0.2 | % | |
| Viscosity Number 3 3 | ISO 307 | 112 | cm³/g | |
| Shrinkage Mold Shrinkage 4 4 | MD：自由的 free, longitudinal | 0.5 | % | |
| Shrinkage Mold Shrinkage 4 5 | TD：自由的 free, transverse | 1.4 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6200 | Mpa | |
| Tensile Strength Tensile Strength | Break Break | ISO 527-2 | 100 | Mpa |
| Tensile strain | Break Break | ISO 527-2 | 3.5 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Automotive Materials Automotive Materials | > 1.00 mm > 1.00 mm | FMVSS 302 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrical performance | 体积电阻率 Volume Resistivity | IEC 60093 | 10000000000000 | ohms·cm |
| Relative permittivity | 100 Hz 100 Hz | IEC 60250 | 0.0012 | |
| 1 MHz 1 MHz | IEC 60250 | 0.015 | ||
| Dissipation factor | 100 Hz 100 Hz | IEC 60250 | 0.00037 | |
| 1 MHz 1 MHz | IEC 60250 | 0.00037 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap | 23℃ 23℃ | ISO 179/1eA | 5.5 | kJ/m² |
| Impact strength of simply supported beam without notch | 23℃ 23℃ | ISO 179/1eU | 41 | kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | 0.80 mm 0.8 mm | UL 94 | HB | |
| 1.60 mm 1.6 mm | UL 94 | HB |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa，Unannealed 66 psi, Unannealed | ISO 75-2/B | 220 | °C |
| 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 200 | °C | |
| Melting temperature | ISO 11357-3 | 223 | °C | |
| Linear coefficient of thermal expansion | MD：23~80℃ MD：23 to 80℃ | ISO 11359-2 | 0.000040 | 1/℃ |
| Maximum operating temperature | short cycle operation short cycle operation | 210 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.