PBT Cristin® SK645FR NC010 DUPONT USA
128
- Unit Price:
- $3516 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 73.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced Filler: Glass fiber reinf 20% filler by weight
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.71 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Top out temperature | 170 | °C | ||
| Shrinkage rate | TD2 | ISO294-4 | 1.5 | % |
| TD | ISO294-4 | 1.2 | % | |
| MD | ISO294-4 | 0.30 | % | |
| MD2 | ISO294-4 | 0.50 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.30 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.10 | % | |
| MediumDensity | 1.49 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1600 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K | ||
| Shrinkage rate | MD | ISO294-4 | 0.50 | % |
| MD2 | ISO294-4 | 0.60 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.32 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.13 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 8300 | Mpa | |
| Tensile stress | Break | ISO527-2 | 110 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.8 | % |
| Bending stress | ISO178 | 165 | Mpa | |
| Tensile modulus | ISO527-2 | 11200 | Mpa | |
| Tensile stress | Break | ISO527-2 | 125 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.4 | % |
| TensileCreepModule | 1hr | ISO899-1 | 11000 | Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 11200 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 215 | kg/cm²(MPa)[Lb/in²] | |
| Tensile creep modulus | 1000hr | ISO899-1 | 8000 | Mpa |
| Bending stress | ISO178 | 215 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 200 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 220 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 210 | °C | |
| Vicat softening temperature | ISO306/B50 | 212 | °C | |
| Melting temperature 5 | ISO11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 39 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.50 | |
| 1MHz | IEC60250 | 3.80 | ||
| Dissipation factor | 100Hz | IEC60250 | 3E-03 | |
| 1MHz | IEC60250 | 0.016 | ||
| Leakage Trace Index | IEC60112 | 250 | V | |
| IEC60112 | 225 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 57 | kJ/m² |
| 23°C | ISO179/1eU | 53 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 40 | kJ/m² |
| 23°C | ISO180/1U | 40 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 50 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 0.75mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 32 | % | |
| FMVSS flammability | FMVSS302 | DNI | ||
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 0.75mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 31 | % | |
| FMVSS flammability | FMVSS302 | DNI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.