PBT Ultradur® B 4040 G4 BK BASF GERMANY
115
- Unit Price:
- $3837 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 49MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant enhanced grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ISO294-4 | 0.40 | % |
| TD | ISO294-4 | 0.90 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Apparent density | 0.70到0.80 | g/cm³ | ||
| Melt volume flow rate | 275°C/2.16kg | ISO1133 | 22.0 | cm3/10min |
| Mold shrinkage 3 | free,longitudinal | 0.21 | % | |
| free,transverse | 1.1 | % | ||
| Stickiness 2 | ISO307 | 105 | cm³/g | |
| Density/specific gravity | ISO1183 | 1.47 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 190 | Mpa | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.8 | % |
| Tensile modulus | ISO527-2 | 7500 | Mpa | |
| Bending modulus | ISO178 | 7010 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 180 | °C | |
| Linear coefficient of thermal expansion | MD：23to80°C | ISO11359-2 | 2.0E-5到3.0E-5 | cm/cm/°C |
| Melting temperature | ISO11357-3 | 223 | °C | |
| specific heat | 1100 | J/kg/°C | ||
| Maximum operating temperature - sortcycle operation | 210 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 3.70 | |
| 1MHz | IEC60250 | 3.50 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 300 | V |
| Dissipation factor | 100Hz | IEC60250 | 1.4E-03 | |
| 1MHz | IEC60250 | 0.018 | ||
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | IEC60093 | 1E+16 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 190 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.75mm | IEC60695-11-10,-20 | HB | |
| 1.6mm | IEC60695-11-10,-20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.