PBT CELANEX® 3309HR CELANESE USA
120
- Unit Price:
- $4192 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 34.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic and electrical Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.70to0.90 | % |
| MD | ISO294-4 | 0.30to0.50 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.16 | % |
| Density/specific gravity | ASTMD792 | 1.53 | g/cm³ | |
| ISO1183 | 1.54 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 9200 | Mpa | |
| Tensile strength | Break,23°C | ASTMD638 | 137 | Mpa |
| Tensile stress | Break | ISO527-2/1A/5 | 139 | Mpa |
| elongation | Break,23°C | ASTMD638 | 2.8 | % |
| Tensile strain | Break | ISO527-2/1A/5 | 2.7 | % |
| Bending modulus | 23°C | ISO178 | 8700 | Mpa |
| Bending stress | 23°C | ISO178 | 210 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 225 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Glass transition temperature 2 | ISO11357-2 | 60.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 220 | °C | |
| Melting temperature 2 | ISO11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 31 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.50 | |
| 1MHz | IEC60250 | 4.10 | ||
| Dissipation factor | 100Hz | IEC60250 | 2.2E-03 | |
| 1MHz | IEC60250 | 0.016 | ||
| Leakage Trace Index | IEC60112 | 425 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.5 | kJ/m² |
| 23°C | ISO179/1eA | 8.5 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 45 | kJ/m² |
| 23°C | ISO179/1eU | 46 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 12 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 35 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.70mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.