PBT CELANEX® 3201 CELANESE USA
134
- Unit Price:
- $4151 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High toughness Hydrolysis resistance Thermal stability Weather resistance UV resistance Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.41 | g/cm³ | |
| ISO1183 | 1.42 | g/cm³ | ||
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 17.0 | cm3/10min |
| Shrinkage rate | MD | ASTMD955 | 0.50to0.70 | % |
| MD | ISO294-4 | 0.50to0.70 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 6000 | Mpa | |
| Tensile strength | Break,23°C | ASTMD638 | 93.1 | Mpa |
| Tensile stress | Break | ISO527-2/1A/5 | 100 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Tensile strain | Break | ISO527-2/1A/5 | 3.5 | % |
| Bending modulus | 23°C | ISO178 | 5600 | Mpa |
| Bending stress | 23°C | ISO178 | 160 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 213 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 218 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 192 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 195 | °C | |
| Glass transition temperature | ISO11357-2 | 60.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 220 | °C | |
| Peak melting temperature | ASTMD3418 | 225 | °C | |
| Melting temperature 2 | ISO11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 3.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTMD257 | 1E+15 | ohms·cm | |
| Dielectric strength 3 | ASTMD149 | 18 | KV/mm | |
| Dielectric constant | 1kHz | ASTMD150 | 3.50 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.5 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 7.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | -- | UL94 | HB | |
| 0.9mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.