PBT Cristin® ST820 BK503 DUPONT USA
111
- Unit Price:
- $4047 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance
- Application Areas:Electronic and electrical
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1220 | ||
| Molding shrinkage rate | ASTM D955 | 1.7 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | -，平行Flow | cm/cm | ASTM D955 | |
| -，垂直Flow | cm/cm | ASTM D955 | ||
| TD | ISO294-4 | 1.7 | % | |
| MD | ISO294-4 | 1.8 | % | |
| Top out temperature | 170 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | >50 | % | |
| Non notched impact strength | -，-40 ℃, 0.00 mm | J/m | ASTM D256 | No Break |
| -，23 ℃, 0.00 mm | J/m | ASTM D256 | No Break | |
| Across Flow | 23℃, 0.00 mm, Compression Molded, Type I | % | ASTM D638 | 150 |
| Bending stress | ISO178 | 50.0 | Mpa | |
| Gap impact strength | 23℃, 0.00 mm, 0.0 mm, Injection Molded, Method A, Across Flow | J/m | ASTM D256 | No Break |
| Tensile stress | Yield | ISO527-2 | 36.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 7.0 | % |
| elongation at break | ASTM D638/ISO 527 | 130 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 1600 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 1600 | Mpa | ||
| Bending modulus | 23 ℃, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant | MPa | ASTM D790 | 1680 |
| ISO178 | 1500 | Mpa | ||
| bending strength | 23 ℃, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I | MPa | ASTM D790 | 53 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 100 | °C |
| 0.45MPa,Annealed | ISO75-2/B | 145 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 50.0 | °C | |
| ASTM D648/ISO 75 | 100 | ℃（℉） | ||
| ASTM D648/ISO 75 | 145 | ℃（℉） | ||
| melting point | 225 | ℃（℉） | ||
| ℃ | DSC | 225 | ||
| Melting temperature 2 | ISO11357-3 | 225 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Burning rate 3 | 1.00mm | ISO3795 | 38 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.