PBT Toraycon® 5107G TORAY JAPAN
112
- Unit Price:
- $2860 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 62MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Fast forming cycle
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate 2 | TD: 3.00 mm | Internal Method | 1.0 | % |
| MD: 3.00 mm | Internal Method | 0.40 | % | |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 0.080 | % |
| Flow Length 3 | 250℃, 1.00 mm | Internal Method | 7.00 | CM |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 | % |
| MD:3.00mm4 | 内部方法 | 0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.080 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 8400 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 125 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ISO178 | 7900 | Mpa |
| Bending stress | 23°C | ISO178 | 195 | Mpa |
| Tensile modulus | 23℃ | ISO 527-2 | 8400 | Mpa |
| Tensile stress | Yield, 23℃ | ISO 527-2 | 125 | Mpa |
| Tensile strain | Break, 23℃ | ISO 527-2 | 3.0 | % |
| Bending modulus | 23℃ | ISO 178 | 7900 | Mpa |
| bending strength | 23℃ | ISO 178 | 195 | Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 12 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 208 | °C |
| Linear expansion coefficient - flow | -30 to 100℃ | ISO 11359-2 | 0.000042 | cm/cm/℃ |
| UL flame retardant rating | UL 94 | HB | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 208 | °C |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 4.2E-05 | cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength4 | 250°C,1.00mm | 内部方法 | 7.00 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.