PBT VALOX™ V4860HR SABIC INNOVATIVE US
111
- Unit Price:
- $9307 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Glass fiber reinforced
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to1.0 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.060 | % |
| Saturation,23°C | ISO62 | 0.19 | % | |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 18 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 12.4 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.64 | g/cm³ | |
| ISO1183 | 1.64 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fracture bending strain 8 | ISO178 | 2.9 | % | |
| Bending stress 5 | --6 | ISO178 | 182 | Mpa |
| --7 | ISO178 | 183 | Mpa | |
| Tensile modulus | ISO527-2/1 | 9450 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 2.3 | % |
| Bending modulus 5 | ISO178 | 7880 | Mpa | |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 2.96 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 2.3 | % |
| Tensile modulus 2 | ASTMD638 | 9750 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 116 | Mpa |
| Break | ASTMD638 | 115 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 6740 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 174 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 111 | Mpa |
| Yield | ISO527-2/5 | 112 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 2.1 | % |
| Break | ISO527-2/5 | 2.2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 2.4E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 2.3E-05 | cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 221 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 197 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 205 | °C | |
| Vicat softening temperature | ASTMD152512 | 176 | °C | |
| -- | ISO306/B50 | 176 | °C | |
| -- | ISO306/B120 | 175 | °C | |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 188 | °C |
| BallPressureTest13 | 75°C | IEC60695-10-2 | Pass |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 74 | J/m |
| 23°C | ASTMD256 | 90 | J/m | |
| CharpyNotchedImpactStrength9 | 23°C | ISO179/1eA | 11 | kJ/m² |
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 8.5 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 13.4 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.8mm,TestingbySABIC | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.