PBT Zytel® LW9030FR BK851 DUPONT SHENZHEN
129
- Unit Price:
- $3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low warpage Flame retardant Filler: Glass fiber reinf 30% filler by weight 30% filler by weight
- Application Areas:Electronic and electrical
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | -，Across Flow | % | ISO 294-4 | 0.65 |
| -，Flow | % | ISO 294-4 | 0.25 | |
| Density/specific gravity | g/cm | ISO 1183 | 1.44 | |
| Shrinkage rate | MD | ISO294-4 | 0.20 | % |
| MD:80°C,48hr | ISO294-4 | 0.15 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.72 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.24 | % | |
| -，23C/59RH | % | ISO 62 | 0.24 | |
| -，Sat/23C | % | ISO 62 | 0.72 | |
| Density/specific gravity | ISO1183 | 1.44 | g/cm³ | |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 0.70 | % |
| TD:80°C,48hr | ISO294-4 | 0.20 | % | |
| MediumDensity | 1.28 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1900 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy non notched impact strength | -，23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | |
| Charpy notch impact strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 9.3 |
| -，23℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | ||
| Non notched impact strength | 23 °C, Type 1 | KJ/m | ISO 180 | |
| Gap impact strength | 23℃, Type 1, Notch A | KJ/m | ISO 180 | |
| Tensile modulus | ISO527-2 | 9500 | Mpa | |
| Tensile stress | Break | ISO527-2 | 130 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.5 | % |
| TensileCreepModule | 1hr | ISO899-1 | 9000 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 7300 | Mpa |
| Bending modulus | ISO178 | 8500 | Mpa | |
| Bending stress | ISO178 | 190 | Mpa | |
| Fracture point tensile stress | 23℃ | MPa | ISO 527-1, -2 | 130 |
| Fracture point tensile strain | 23℃ | % | ISO 527-1, -2 | 2.5 |
| Tensile creep modulus | -，1h | MPa | ISO 899-1 | 9000 |
| -，1000h | MPa | ISO 899-1 | 7300 | |
| Tensile modulus | 23℃ | MPa | ISO 527-1, -2 | 9500 |
| bending strength | 23℃ | MPa | ISO 178 | 190 |
| Charpy non notched impact strength | -，-30 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 66 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Linear coefficient of thermal expansion | 平行Flow ，23 to 55°C (73 to 130°F) | cm/cm/°C | ISO 11359-1, -2 | |
| 垂直Flow ，23 to 55°C (73 to 130°F) | cm/cm/°C | ISO 11359-1, -2 | 0.000025 | |
| Hot deformation temperature | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 215 |
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 182 | |
| 0.45MPa,Unannealed | ISO75-2/B | 215 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 170 | °C | |
| Glass transition temperature 2 | ISO11357-2 | 120 | °C | |
| Vicat softening temperature | ISO306/B50 | 150 | °C | |
| Melting temperature 2 | ISO11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Flame retardancy | -，1.50 mm | UL 94 | HB | |
| -，3.00 mm | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 36 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.60 | ||
| Dissipation factor | 100Hz | IEC60250 | 2.4E-03 | |
| 1MHz | IEC60250 | 0.017 | ||
| Leakage Trace Index | IEC60112 | 425 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 65 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 8.0 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 50 | kJ/m² |
| 23°C | ISO180/1U | 50 | kJ/m² |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | % | ISO 4589-1, -2 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 42 | mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 90.0 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.