PBT Cristin® T841FR DUPONT USA
120
- Unit Price:
- $3481 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact Filler: Glass fiber reinf 10% filler by weight
- Application Areas:Electronic and electrical Home appliance accessorie auto parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| Shrinkage rate | TD | ISO294-4 | 1.2 | % |
| MD | ISO294-4 | 0.70 | % | |
| MediumDensity | 1.31 | g/cm³ | ||
| Top out temperature | 150 | °C | ||
| SpecificHeatCapacity of Melt | 1970 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.23 | W/m/K | ||
| Melt viscosity | 250°C,1000sec^-1 | ISO11443 | 240000 | mPa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 3000 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 2000 | Mpa |
| Tensile stress | Break | ISO527-2 | 70.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 4.7 | % |
| Tensile modulus | ISO527-2 | 3900 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 170 | °C |
| 8.0MPa,Unannealed | ISO75-2/C | 66.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 180 | °C | |
| Melting temperature 2 | ISO11357-3 | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.018 | ||
| Dielectric strength | IEC60243-1 | 27 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.80 | ||
| Leakage Trace Index | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 46 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 0.75mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 30 | % | |
| FMVSS flammability | FMVSS302 | DNI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.