PBT VALOX™ 508-7001 SABIC INNOVATIVE US
128
Unit Price:$3967 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 26.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 1.50 to 3.20 mm | 内部方法 | 0.30 到 0.50 | % |
| Flow : 3.20 to 4.60 mm | 内部方法 | 0.50 到 0.80 | % | |
| Across Flow : 1.50 to 3.20 mm | 内部方法 | 0.40 到 0.60 | % | |
| Across Flow : 3.20 to 4.60 mm | 内部方法 | 0.60 到 0.90 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 | % |
| Specific volume | ASTM D792 | 0.660 | cm³/g | |
| Outdoor applicability | UL 746C | f2 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | 50.0 mm Span | ASTM D790 | 6890 | Mpa |
| bending strength | Break, 50.0 mm Span | ASTM D790 | 189 | Mpa |
| Tensile strength | Break | ASTM D638 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL 746 | 125 | °C | |
| RTI Imp | UL 746 | 110 | °C | |
| RTI Elec | UL 746 | 125 | °C | |
| Linear coefficient of thermal expansion - flow | -40 to 40°C | ASTM E831 | 2.3E-5 | cm/cm/°C |
| 60 to 138°C | ASTM E831 | 1.6E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 215 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 176 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 | ||
| High arc combustion index (HAI) 5 | UL 746 | PLC 3 | ||
| Dielectric constant | 100 Hz | ASTM D150 | 3.60 | |
| 1 MHz | ASTM D150 | 3.60 | ||
| Volume resistivity | ASTM D257 | 5.9E+16 | ohms·cm | |
| Dissipation factor | 100 Hz | ASTM D150 | 1.4E-3 | |
| 1 MHz | ASTM D150 | 0.020 | ||
| Dielectric strength | 1.60 mm, in Oil | ASTM D149 | 29 | KV/mm |
| 3.20 mm, in Air | ASTM D149 | 24 | KV/mm | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Arc resistance 4 | ASTM D495 | PLC 6 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 250 到 265 | °C | ||
| Mold temperature | 65 到 90 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 40 到 80 | % | ||
| Temperature at the rear of the barrel | 240 到 255 | °C | ||
| Temperature in the middle of the barrel | 245 到 260 | °C | ||
| Temperature at the front of the material cylinder | 250 到 265 | °C | ||
| Spray nozzle temperature | 245 到 260 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 50 到 80 | rpm | ||
| Exhaust hole depth | 0.025 到 0.038 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 6.00 | J |
| 23°C, Total Energy | ASTM D3763 | 8.00 | J | |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 640 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 119 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.