PBT Crastin® S620F20 DuPont, European Union
98
- Unit Price:
- $3286 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO1183 | 1.31 | g/cm³ | |
| Melt mass flow rate | 250°C/2.16kg | ISO1133 | 19 | g/10min |
| Shrinkage rate | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.7 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| Stickiness number | ISO307 | 130 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2600 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 59.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 8.0 | % |
| Nominal tensile fracture strain | ISO527-2 | 30 | % | |
| Tensile creep modulus | 1hr | ISO899-1 | 2600 | Mpa |
| 1000hr | ISO899-1 | 1800 | Mpa | |
| Bending stress | ISO178 | 88.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 0.45MPa,Annealed | ISO75-2/B | 180 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 60.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 60.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 175 | °C | |
| Melting temperature 3 | ISO11357-3 | 225 | °C | |
| Crystallization peak temperature 3 | ISO11357-3 | 192 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 26 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| 1MHz | IEC60250 | 3.20 | ||
| Dissipation factor | 100Hz | IEC60250 | 2E-03 | |
| 1MHz | IEC60250 | 0.020 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt density | 1.11 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 2100 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 | kJ/m² |
| 23°C | ISO179/1eA | 4.5 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 4.0 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 70 | kJ/m² |
| 23°C | ISO180/1U | 140 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94,IEC60695-11-10,-20 | HB | |
| 1.5mm | UL94,IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 22 | % | |
| FMVSS flammability | FMVSS302 | SE/NBR |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.