| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.67 | |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | | ISO527-2 | 47.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 1.8 | % |
| Bending stress | | ISO178 | 84.0 | Mpa |
| tensile strength | | ASTM D638/ISO 527 | 47 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ASTM D790/ISO 178 | 4360 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ISO178 | 4360 | Mpa |
| bending strength | | ASTM D790/ISO 178 | 84 | kg/cm²(MPa)[Lb/in²] |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | 1.8 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility (rate) | | UL94 | V-0 | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 90.0 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 7 | mm/mm.℃ |
| Linear coefficient of thermal expansion | MD：23to55°C | 内部方法 | 7E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | 3.00mm | IEC60243-1 | 15 | KV/mm |
| Leakage Trace Index | | IEC60112 | 225 | V |
| Volume resistivity | | IEC60093 | 2E+15 | ohms·cm |
| Volume resistivity | | ASTM D257/IEC 60093 | 2.0 x 10^15 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 65 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ColourNumber | | | EF2001/ED3002 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.