PBT CELANEX® 4612R CELANESE USA
126
- Unit Price:
- $4109 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Electronic and electrical Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume ratio | ISO 1133 | 8.5 | CM | |
| Shrinkage rate | Across Flow | ISO 294-4 | 0.6-0.8 | % |
| Across Flow | ISO 294-4 | 1.2-1.4 | % | |
| Water absorption rate | 23℃ | ISO 62 | 0.45 | % |
| 23℃,50%相对湿度 | ISO 62 | 0.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 1mm/min | ISO 527-2/1A | 2800 | Mpa |
| Yield stress | 50mm/min | ISO 527-2/1A | 50 | Mpa |
| Yield modulus | 50mm/min | ISO 527-2/1A | 4 | % |
| tensile strength | 5mm/min | ISO 527-2/1A | 45 | Mpa |
| Bending modulus | 23℃ | ISO 178 | 2700 | Mpa |
| bending strength | 23℃ | ISO 178 | 75 | Mpa |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 60 | KJ/m |
| -30℃ | ISO 179/1eU | 50 | KJ/m | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 14 | KJ/m |
| -30℃ | ISO 179/1eA | 5 | KJ/m | |
| IZOD notch impact strength | 23℃ | ISO 180/1A | 13 | KJ/m |
| Rockwell hardness | ISO 2039-2 | 111 | M |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO 11357-1,-2,-3 | 225 | °C | |
| Glass transition temperature | ISO 11357-1,-2,-3 | 60 | °C | |
| Hot deformation temperature | 1.8Mpa | ISO 75-1/-2 | 92 | °C |
| 0.45Mpa | ISO 75-1/-2 | 200 | °C | |
| Vicat softening temperature | ISO 306 | 170 | °C | |
| Coefficient of linear expansion | Across Flow | ISO 11359-2 | 0.4 | E-4/℃ |
| Across Flow | ISO 11359-2 | 1.38 | E-4/℃ | |
| Flame retardancy | UL94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative resistivity | 100Hz | IEC 60250 | 4.3 | |
| 1MHz | IEC 60250 | 3.8 | ||
| Dielectric dissipation factor | 100Hz | IEC 60250 | 60 | E-4 |
| 1MHz | IEC 60250 | 290 | E-4 | |
| Volume resistivity | IEC 60093 | ＞1E12 | ohm.m | |
| Surface resistivity | IEC 60093 | ＞1E14 | Ohm | |
| Dielectric strength | IEC 60243-1 | 26 | KV/mm | |
| Relative Trace Index | IEC 60112 | 425 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.