PBT Ultradur® B 4406 G3 BASF GERMANY
165
Unit Price:$3569 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 83MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant High mobility
- Application Areas:Thin walled components Switch panel Shell Electrical components Laptop case
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| Viscosity value | 降低的粘度 | ISO1628 | 116.0 | ml/g |
| Density/specific gravity | ISO1183 | 1.55 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 6.5 | kJ/m² |
| 23°C | ISO179 | 6.5 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180 | 6.1 | kJ/m² |
| 23°C | ISO180 | 6.1 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 32 | kJ/m² |
| Tensile modulus | 23°C | ISO527-2 | 6500 | Mpa |
| Bending modulus | 23°C | ISO178 | 6050 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 110 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 2.7 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | 3.0mm | UL746 | 140 | °C |
| 0.40mm | UL746 | 75.0 | °C | |
| 0.75mm | UL746 | 140 | °C | |
| 1.5mm | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | 0.40mm | UL746 | 75.0 | °C |
| 0.75mm | UL746 | 130 | °C | |
| 1.5mm | UL746 | 130 | °C | |
| 3.0mm | UL746 | 130 | °C | |
| RTIStr | 0.40mm | UL746 | 75.0 | °C |
| 0.75mm | UL746 | 125 | °C | |
| 1.5mm | UL746 | 130 | °C | |
| 3.0mm | UL746 | 130 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 217 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 195 | °C | |
| Melting temperature (DSC) | ISO3146 | 223 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+13 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | V-0 | |
| 0.75mm | UL94 | V-0 | ||
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | V-05VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.