PBT CELANEX® 3216 CELANESE USA

118

Unit Price:
$4116 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant
Application Areas:Connector
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.40to0.60	%
	Shrinkage rate	TD	ISO294-4	1.1	%
	Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.30to0.60	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.17	%
Density/specific gravity		ASTMD792	1.54	g/cm³
Density/specific gravity	Density/specific gravity		ISO1183	1.54	g/cm³
Melt volume flow rate	250°C/2.16kg	ISO1133	9.00	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2/1A/1	6700	Mpa
Tensile strength	Break,23°C	ASTMD638	100	Mpa
Tensile stress	Break	ISO527-2/1A/5	100	Mpa
elongation	Break,23°C	ASTMD638	4.0	%
Tensile strain	Break	ISO527-2/1A/5	3.0	%
Bending modulus	23°C	ISO178	6000	Mpa
Bending stress	23°C	ISO178	155	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	217	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTMD648	213	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	185	°C
			Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	200	°C
			Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	95.0	°C
Glass transition temperature 2		ISO11357-2	60.0	°C
Vicat softening temperature		ISO306/B50	206	°C
Peak melting temperature		ASTMD3418	225	°C
Melting temperature 2		ISO11357-3	225	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	3.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+15	ohms
Volume resistivity		ASTMD257	2E+16	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	1E+15	ohms·cm
Dielectric strength 3		ASTMD149	26	KV/mm
Dielectric strength		IEC60243-1	30	KV/mm
Dielectric constant	1MHz	ASTMD150	3.20
Relative permittivity	100Hz	IEC60250	3.70
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.50
Dissipation factor	1MHz	ASTMD150	0.010
	Dissipation factor	100Hz	IEC60250	3.3E-03
	Dissipation factor	Dissipation factor	1MHz	IEC60250	0.016
Arc resistance		ASTMD495	79.0	sec
Leakage Trace Index		ASTMD3638	250	V
Leakage Trace Index	Leakage Trace Index		IEC60112	250	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	6.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	28	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	28	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO180/1A	5.5	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ISO2039-2	87

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Extreme Oxygen Index		ISO4589-2	27to32	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.