PBT CELANEX® 2002 CELANESE USA
108
- Unit Price:
- $3119 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Good flexibility Glass fiber reinforced
- Application Areas:Electrical field Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.8-2.0 | % | |
| Water absorption rate | 23℃,Saturation | ISO 62 | 0.09 | % |
| Melt volume ratio | ISO 1133 | 20 | CM | |
| Oxygen index | ISO 4589 | 22 | % | |
| Density/specific gravity | ISO 1183 | 1310 | kg/m |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched impact strength of simply supported beams | -，23℃ | ISO 179/1eU | NB | KJ/m |
| -，-30℃ | ISO 179/1eU | 190 | KJ/m | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 5.0 | KJ/m |
| Yield stress | 50mm/min | ISO 527-2/1A | 60 | Mpa |
| Yield modulus | 50mm/min | ISO 527-2/1A | 4 | % |
| Charpy Notched Impact Strength | -，23℃ | ISO 179/1eA | 6 | KJ/m |
| -，-30℃ | ISO 179/1eA | 6 | KJ/m | |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 2600 | Mpa |
| tensile strength | ISO 527-2/1A | 60 | Mpa | |
| Rockwell hardness | ISO 2039-2 | 78 | M | |
| Bending modulus | 23℃ | ISO 178 | 2500 | Mpa |
| bending strength | 23℃ | ISO 178 | 80 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，1.8Mpa | ISO 75-1/-2 | 55 | °C |
| -，0.45Mpa | ISO 75-1/-2 | 150 | °C | |
| Vicat softening temperature | ISO 306 | 190 | °C | |
| Flame retardancy | UL94 | HB | ||
| Melting temperature | ISO 11357-1,-2,-3 | 225 | °C | |
| Coefficient of linear expansion | -，Across Flow | ISO 11359-2 | 1.1 | E-4/℃ |
| -，Across Flow | ISO 11359-2 | 1.27 | E-4/℃ | |
| Glass transition temperature | ISO 11357-1,-2,-3 | 60 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric dissipation factor | -，100Hz | IEC 60250 | 14 | E-4 |
| -，1MHz | IEC 60250 | 220 | E-4 | |
| Relative resistivity | -，100Hz | IEC 60250 | 4 | |
| -，1MHz | IEC 60250 | 3.5 | ||
| Relative Trace Index | IEC 60112 | 600 | ||
| Dielectric strength | IEC 60243-1 | 23 | KV/mm | |
| Surface resistivity | IEC 60093 | 1E+15 | Ohm | |
| Volume resistivity | IEC 60093 | 1E+13 | ohm.m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.