PBT DURANEX® 2002 JAPAN POLYPLASTIC
146
- Unit Price:
- $4000 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Good flexibility Glass fiber reinforced Friction resistance
- Application Areas:Electrical field Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 792 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | ASTMD1238 | 20 | g/10min | |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 18.0 | cm3/10min |
| flow | ASTMD955 | 1.8到2.0 | % | |
| Vertical flow direction | ISO294-4 | 1.8到2.0 | % | |
| Flow direction | ISO294-4 | 1.8到2.0 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.19 | % |
| 23°C,24hr | ISO62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | ISO527-2 | 57.0 | Mpa | |
| Nominal tensile fracture strain | ISO527-2 | 12 | % | |
| Bending modulus | ISO178 | 3100 | Mpa | |
| Bending stress | ISO178 | 95.0 | Mpa | |
| tensile strength | ISO 527-1/-2 | 57 | Mpa | |
| bending strength | ISO 178 | 95 | Mpa | |
| Bending modulus | ISO 178 | 3100 | Mpa | |
| Charpy notch impact strength | ISO 179/1eA | 3.2 | kJ/m² | |
| 50% strain | ISO527-2/1A/50 | 30.0 | Mpa | |
| Surrender- 40°C | ASTMD638 | 7.2 | % | |
| Yield, 0 ° C | ASTMD638 | 4.4 | % | |
| Surrender, 23 ° C | ASTMD638 | 3.2 | % | |
| Yield, 80 ° C | ASTMD638 | 17 | % | |
| Yield, 121 ° C | ASTMD638 | 23 | % | |
| yield | ISO527-2/1A/50 | 4.0 | % | |
| Fracture, 23 ° C | ASTMD638 | 200 | % | |
| crack | ISO527-2/1A/50 | 220 | % | |
| Nominal tensile fracture strain | ISO527-2/1A/50 | >50 | % | |
| Bending modulus | ASTM D-790 | 2540 | Mpa | |
| tensile strength | ASTM D-638 | 51 | Mpa | |
| crack | ISO527-2/1A/50 | 35.0 | Mpa | |
| Bending modulus | 23°C | ISO178 | 2500 | Mpa |
| Bending stress | 23°C | ISO178 | 80.0 | Mpa |
| elongation at break | ASTM D638/ISO 527 | >200 | % | |
| tensile strength | ASTM D638/ISO 527 | 51 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2540 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 85 | kg/cm²(MPa)[Lb/in²] | |
| Surrender- 40°C | ASTMD638 | 101 | Mpa | |
| Yield, 0 ° C | ASTMD638 | 75.8 | Mpa | |
| Surrender, 23 ° C | ASTMD638 | 55.8 | Mpa | |
| Yield, 80 ° C | ASTMD638 | 24.8 | Mpa | |
| Yield, 121 ° C | ASTMD638 | 17.9 | Mpa | |
| yield | ISO527-2/1A/50 | 60.0 | Mpa | |
| elongation | ASTM D-638 | >200 | % | |
| bending strength | ASTM D-790 | 85 | Mpa | |
| IZOD impact strength | ASTM D-256 | 34 | J/m | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 34 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8Mpa | ISO 75-1/-2 | 80 | °C |
| Flame retardancy | UL94 | HB | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 80.0 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | 内部方法 | 9E-05 | cm/cm/°C |
| TD：23to55°C | 内部方法 | 9E-05 | cm/cm/°C | |
| Glass transition temperature | ISO11357-2 | 60.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 190 | °C | |
| Melting temperature | ISO11357-3,ASTMD3418 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.4E-04 | cm/cm/°C | |
| Hot deformation temperature | ASTM D648/ISO 75 | 70 | ℃（℉） | |
| 1.82Mpa | ASTM D-648 | 70 | °C | |
| Flame retardancy | UL 94 | HB | ||
| 0.45MPa, unannealed | ASTMD648 | 160 | °C | |
| ISO75-2/B | 150 | °C | ||
| 1.8MPa, unannealed | ASTMD648,ISO75-2/A | 55.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1MHz | ASTMD150 | 3.20 | ||
| 100Hz | IEC60250 | 4.00 | ||
| 1MHz | IEC60250 | 3.50 | ||
| Dissipation factor | 100Hz | IEC60250 | 1.4E-03 | |
| 1MHz | IEC60250 | 0.022 | ||
| Leakage Trace Index | IEC60112 | 600 | V | |
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| -- | ASTMD257 | 1E+16 | ohms·cm | |
| IEC60093 | 1E+15 | ohms·cm | ||
| --1 | ASTMD149 | 17 | KV/mm | |
| -- | IEC60243-1 | 23 | KV/mm | |
| Dielectric strength | 3.00mm | IEC60243-1 | 17 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 190 | kJ/m² |
| 23°C | ISO179/1eU | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 85 | |
| M-Sale | ISO2039-2 | 78 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB | ||
| 0.710mm | UL94 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 22 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ColourNumber | EF2001/ED3002 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.