Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.40 | % |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.2 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress | 23°C | ISO178 | 210 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 140 | Mpa |
| Friction coefficient 4 | | | 0.20 | |
| Friction coefficient vs. Metal5 | | SuzukiMethod | 0.15 | |
| Bending modulus | 23°C | ISO178 | 11000 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 2.4 | % |
| Tensile modulus | 23°C | ISO527-2 | 11700 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 4E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 207 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor 6 | 23°C,1MHz | IEC60250 | 0.020 | |
| Arc resistance 7 | | IEC60950 | 134 | sec |
| Dielectric strength | | IEC60243-1 | 14 | KV/mm |
| Dielectric constant 5 | 23°C,50Hz | IEC60250 | 4.00 | |
| Dissipation factor 6 | 23°C,50Hz | IEC60250 | 1E-03 | |
| Volume resistivity | | IEC60093 | 1.1E+17 | ohms·cm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Dielectric constant 5 | 23°C,1kHz | IEC60250 | 3.80 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale,23°C | ISO2039-2 | 85 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| BarFlowLength8 | 250°C,1.00mm | 内部方法 | 145 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.