PBT DURANEX® 2000 JAPAN POLYPLASTIC

130

Unit Price:
$3136 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant
Application Areas:Electrical tools Lighting fixtures
Color:--
Grade:Flame retardant grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.31

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	23°C,24hr	ISO62	0.20	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress		ISO527-2	60.0	Mpa
Nominal tensile fracture strain		ISO527-2	20	%
Bending modulus		ISO178	2500	Mpa
Bending stress		ISO178	89.0	Mpa
tensile strength		ASTM D638/ISO 527	60	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2500	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	89	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D527-1,2	60	Mpa
Tensile failure strain		ASTM D527-1,2	20	%
bending strength		ASTM D178	89	Mpa
Bending modulus		ASTM D178	2500	Mpa
Charpy notch impact strength		ASTM D179/1eA	3.2	kJ/m²
Load bending temperature	1.8Mpa	ASTM D75-1,2	73	°C
Tensile elongation at break (elongation at break)		ASTM D638/ISO 527	20	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Coefficient of linear expansion		ASTM D11359	10	×10-5/℃
Flame retardancy		UL94	HB
Combustibility (rate)		UL94	HB
Linear expansion coefficient		ASTM D696/ISO 11359	10	mm/mm.℃
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	73.0	°C
Linear coefficient of thermal expansion	MD：23to55°C	内部方法	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	内部方法	1.1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	5E+16	ohms·cm
Dielectric strength	3.00mm	IEC60243-1	17	KV/mm
Volume resistivity		ASTM D257/IEC 60093	5.0 x 10^16	Ω.cm
Volume resistivity	Volume resistivity		IEC 60093	5×1016	Ω.cm
Surface resistivity		IEC 60093	7×1016	Ω

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ISO2039-2	90

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ColourNumber			EF2001/PLT9908

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.