| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.020 | % |
| flow | | ASTMD955 | 1.0到1.2 | % |
| Vertical flow direction | | ISO294-4 | 1.5到1.8 | % |
| Flow direction | | ISO294-4 | 1.2到1.5 | % |
| Lateral flow | | ASTMD955 | 0.80到1.0 | % |
| -- | | ASTMD792 | 1.40 | g/cm³ |
| -- | | ISO1183 | 1.35 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Break | ISO527-2/1A/5 | 90.0 | Mpa |
| Tensile strain | Break | ISO527-2/1A/5 | 8.0 | % |
| Tensile modulus | | ISO527-2/1A/1 | 3500 | Mpa |
| Bending modulus | 23°C | ISO178 | 4200 | Mpa |
| Bending stress | 23°C | ISO178 | 145 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 5.2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 5.3E-05 | cm/cm/°C |
| Melting temperature 2 | | ISO11357-3 | 280 | °C |
| 1.8MPa, unannealed | | ASTMD648 | 104 | °C |
| 1.8MPa, unannealed | | ISO75-2/A | 115 | °C |
| 8.0Mpa, unannealed | | ISO75-2/C | 95.0 | °C |
| Glass transition temperature 1 | | ISO11357-2 | 90.0 | °C |
| 0.45MPa, annealed | | ASTMD648 | 204 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Leakage Trace Index | | IEC60112 | 125 | V |
| --3 | | ASTMD149 | 18 | KV/mm |
| 1kHz | | ASTMD150 | 3.00 | |
| 1kHz | | ASTMD150 | 1E-03 | |
| Arc resistance | | ASTMD495 | 124 | sec |
| 1MHz | | IEC60250 | 4.60 | |
| 1MHz | | ASTMD150 | 9E-04 | |
| 1MHz | | IEC60250 | 1.1E-03 | |
| 1MHz | | ASTMD150 | 3.00 | |
| -- | | ASTMD257 | 1E+07 | ohms·cm |
| -- | | IEC60093 | 1E+11 | ohms·cm |
| -- | | IEC60243-1 | 18 | KV/mm |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| SpecificHeatCapacity of Melt | | 内部方法 | 1830 | J/kg/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO180/1U | 82 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| M-grade | | ASTMD785 | 93 | |
| M scale | | ISO2039-2 | 90 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 3.00mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.