PPS FORTRON® 1131L4 CELANESE USA

124

Unit Price:
$3506 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
100MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced High temperature resistan
Application Areas:Electrical applications Automotive Applications
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	0.50 到 0.80	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.30 到 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break	ISO 527-2/1A/5	165	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.9	%
Tensile modulus		ISO 527-2/1A	12200	Mpa
Bending modulus	23°C	ISO 178	12000	Mpa
Bending stress		ISO 178	255	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.9E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.2E-5	cm/cm/°C
Melting temperature		ISO 11357-3	280	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	265	°C
Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	205	°C
Glass transition temperature 3		ISO 11357-2	90.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm

injection	Test Result	Unit
drying temperature	100 到 110	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	330 到 340	°C
Mold temperature	140 到 160	°C
drying time	3.0 到 4.0	hr
Temperature at the rear of the barrel	290 到 300	°C
Temperature in the middle of the barrel	310 到 320	°C
Temperature at the front of the material cylinder	330 到 340	°C
Spray nozzle temperature	310 到 330	°C
Back pressure	< 3.00	Mpa
Hopper temperature	20 到 30	°C
Injection speed	快速

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	42	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	42	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M -Sale	ISO 2039-2	100

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.