PPS INFINO® EW-2120G Samsung Cheil South Korea
117
- Unit Price:
- $4685 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Filler: Glass fiber reinf 40% filler by weight
- Application Areas:Electronic and electrical Application in the automo
- Color:--
- Grade:Fill level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.27to0.33 | % |
| TD：3.20mm | ASTMD955 | 0.32to0.39 | % | |
| Ash Content | ASTMD5630 | 40 | % | |
| Density/specific gravity | ASTMD792 | 1.66 | g/cm³ | |
| ISO1183 | 1.66 | g/cm³ | ||
| Melt mass flow rate | 316°C/5.0kg | ASTMD1238 | 55 | g/10min |
| 316°C/5.0kg | ISO1133 | 83 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strain | Break | ISO527-2/5 | 2.7 | % |
| Bending modulus 3 | ASTMD790 | 12700 | Mpa | |
| Bending modulus 4 | ISO178 | 13400 | Mpa | |
| Bending strength 3 | ASTMD790 | 265 | Mpa | |
| Bending stress 4 | ISO178 | 260 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 6860 | Mpa | |
| Tensile modulus | ISO527-2/5 | 11400 | Mpa | |
| Tensile strength 2 | Yield | ASTMD638 | 186 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 180 | Mpa |
| Tensile strength 2 | Break | ASTMD638 | 177 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 180 | Mpa |
| Elongation rate 2 | Break | ASTMD638 | 3.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 282 | °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 283 | °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 283 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 270 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 267 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 272 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 13 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTMD256 | 98 | J/m |
| 23°C,6.35mm | ASTMD256 | 85 | J/m | |
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 11 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 121 | |
| R-Scale | ASTMD785 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.9mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.