PPS FORTRON® 1342L4 CELANESE USA
116
- Unit Price:
- $5574 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 29MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High temperature resistan Filler fiberglass reinfo
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Halogen-free flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | -- | ASTMD792 | 1.70 | g/cm³ |
| -- | ISO1183 | 1.69 | g/cm³ | |
| Shrinkage rate | MD | ASTMD955 | 0.20到0.30 | % |
| TD | ASTMD955 | 0.50到0.70 | % | |
| TD | ISO294-4 | 0.50 | % | |
| MD | ISO294-4 | 0.20 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 14400 | Mpa | |
| Tensile strength | 断裂,23°C | ASTMD638 | 152 | Mpa |
| elongation | 断裂,23°C | ASTMD638 | 2.0 | % |
| Tensile strength | 断裂 | ISO527-2/1A/5 | 165 | Mpa |
| Wear factor | 416Stainless:32°C | ASTMD3702 | 166 | 10^-10in³·min/ft·lb·hr |
| C-1018Steel:49°C | ASTMD3702 | 323 | 10^-10in³·min/ft·lb·hr | |
| C-1018Steel:93°C | ASTMD3702 | 825 | 10^-10in³·min/ft·lb·hr | |
| elongation | 断裂 | ISO527-2/1A/5 | 1.6 | % |
| Bending modulus | 23°C | ISO178 | 13700 | Mpa |
| Bending stress | ISO178 | 245 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 268 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 270 | °C | |
| 8.0MPa,未退火 | ISO75-2/C | 215 | °C | |
| Glass transition temperature | ISO11357-2 | 90.0 | °C | |
| Melting temperature | ISO11357-3 | 280 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| TD | ISO11359-2 | 4E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.5 | kJ/m² |
| 23°C | ISO179/1eA | 8.5 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 44 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.5 | kJ/m² |
| 23°C | ISO180/1A | 8.5 | kJ/m² |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| SpecimensThickness Shrinkage | 内部方法 | 3.18 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.