PPS FORTRON® 1140L6 BK CELANESE USA

208

Unit Price:
$7826 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Glass fiber reinforced High temperature resistan
Application Areas:Fitness equipment fibre
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity		ISO 1183	1.65	g/cm³
Mold shrinkage rate		ISO 2577	0.2-0.6	%
Specific volume		ASTMD792	0.625	cm³/g
Density/specific gravity		ISO1183	1.65	g/cm³
Melt mass flow rate		ASTMD1238	19	g/10min
Shrinkage rate	MD	ASTMD955	0.20to0.30	%
	Shrinkage rate	TD	ASTMD955	0.50to0.70	%
		Shrinkage rate	TD	ISO294-4	0.40to0.60	%
		Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.20to0.60	%
Water absorption rate	Saturation,23°C	ISO62	0.020	%
SpiralFlow		内部方法	21.5
Density/specific gravity		ASTMD792	1.60	g/cm³
SpecificHeatCapacity of Melt		内部方法	1500	J/kg/°C

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break,23°C	ASTMD638	200	Mpa
Tensile stress	Break	ISO527-2/1A/5	195	Mpa
elongation	Break,23°C	ASTMD638	2.0	%
Tensile strain	Break	ISO527-2/1A/5	1.9	%
Bending modulus	23°C	ISO178	14500	Mpa
Bending stress 2		ISO178	285	Mpa
Tensile modulus		ISO527-2/1A/1	14700	Mpa
Tensile modulus	Tensile modulus		ISO 527-1	14700	Mpa
tensile strength		ISO 527-1	195	Mpa
elongation	Break	ISO 527-1	1.9	%
Bending modulus		ISO 178	14500	Mpa
bending strength		ISO 178	285	Mpa
IZOD notch impact strength	23℃	ISO 180/1A	10	kJ/m²
Rockwell hardness		ISO 2039-2	100	M-scale

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.80Mpa	ISO 75-1	270	°C
Flame retardant grade		UL94	V-0
Melting temperature 5		ISO11357-3	280	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	2.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	4.2E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Annealed	ASTMD648	280	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	265	°C
		Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	270	°C
		Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	215	°C
Glass transition temperature 3		ISO11357-2	90.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	>1.0E+15	ohms
Volume resistivity		ASTMD257	1E+16	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric strength 4		ASTMD149	15	KV/mm
Dielectric strength		IEC60243-1	28	KV/mm
Dielectric constant	1kHz	ASTMD150	3.50
Dielectric constant	Dielectric constant	1MHz	ASTMD150	3.50
Relative permittivity	1MHz	IEC60250	4.10
Dissipation factor	1kHz	ASTMD150	1E-03
	Dissipation factor	1MHz	ASTMD150	1E-03
	Dissipation factor	Dissipation factor	1MHz	IEC60250	2E-03
Arc resistance		ASTMD495	134	sec
Leakage Trace Index		IEC60112	125	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of cantilever beam gap	-30°C	ISO180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	10	kJ/m²
Unscented Izod impact strength	23°C	ISO180/1U	34	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	10	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	53	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	53	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTMD785	100
Rockwell hardness	Rockwell hardness	M-Scale	ISO2039-2	100

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	V-0

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate		ISO 62	0.02	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
CSARating	8.40E-7mm	CSAF-1	A00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.