PPS DURAFIDE® 6165A4 HD9050 JAPAN POLYPLASTIC

116

Unit Price:
$5395 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
60MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant wear resistant
Application Areas:Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ASTMD955	0.30to0.50	%
	Shrinkage rate	TD	ISO294-4	0.30to0.70	%
		Shrinkage rate	MD	ISO294-4	0.20to0.60	%
		Shrinkage rate	Shrinkage rate	MD	ASTMD955	0.10to0.20	%
Water absorption rate	Saturation,23°C	ISO62	0.020	%
Mold shrinkage rate		ISO 2577	0.2-0.6	%
Melt mass flow rate		ASTMD1238	7.5	g/10min
SpecificHeatCapacity of Melt		内部方法	1600	J/kg/°C
Specific volume		ASTMD792	0.502	cm³/g
SpiralFlow		内部方法	15.5
Density/specific gravity		ISO 1183	1.95	g/cm³
	Density/specific gravity		ISO1183	1.95	g/cm³
	Density/specific gravity	Density/specific gravity		ASTMD792	2.00	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break	ISO527-2/1A/5	130	Mpa
Tensile strain	Break	ISO527-2/1A/5	1.2	%
Bending stress 2		ISO178	210	Mpa
Tensile strength	Break,23°C	ASTMD638	131	Mpa
IZOD notch impact strength	23℃	ISO 180/1A	6	kJ/m²
Tensile modulus		ISO 527-1	19000	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	19000	Mpa
tensile strength		ISO 527-1	130	Mpa
elongation	Break	ISO 527-1	1.2	%
elongation	elongation	Break,23°C	ASTMD638	1.3	%
Rockwell hardness		ISO 294-4	100	M-scale
Bending modulus		ISO 178	18800	Mpa
Bending modulus	Bending modulus	23°C	ISO178	18800	Mpa
bending strength		ISO 178	210	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.80Mpa	ISO 75-1	270	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTMD648	280	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	266	°C
			Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	270	°C
			Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	215	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	2.4E-05	cm/cm/°C
Flame retardant grade	0.750mm	UL94	V-0
Melting temperature 5		ISO11357-3	280	°C
Glass transition temperature 3		ISO11357-2	90.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	1MHz	IEC60250	5.60
Leakage Trace Index		IEC60112	175	V
Dielectric strength		IEC60243-1	25	KV/mm
Dissipation factor	1kHz	ASTMD150	1E-03
	Dissipation factor	1MHz	ASTMD150	9E-04
	Dissipation factor	Dissipation factor	1MHz	IEC60250	2E-03
Surface resistivity		IEC60093	>1.0E+15	ohms
Dielectric constant	1kHz	ASTMD150	5.40
Dielectric constant	Dielectric constant	1MHz	ASTMD150	5.60
Arc resistance		ASTMD495	182	sec
Volume resistivity		ASTMD257	1E+16	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	>1.0E+17	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	20	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	20	kJ/m²
Unscented Izod impact strength	23°C	ISO180/1U	20	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	7.0	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO180/1A	6.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	6.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ISO2039-2	100
Rockwell hardness	Rockwell hardness	M-Scale	ASTMD785	100

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	V-0
	UL flame retardant rating	1.5mm	UL94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Extreme Oxygen Index		ISO4589-2	53	%

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate	23℃	ISO 62	0.02	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
SpecimensThickness Shrinkage		内部方法	3.18	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.