PPS LNP™ LUBRICOMP™ OCF-100-10MG SABIC INNOVATIVE US
130
- Unit Price:
- $4720 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Filler: Glass fiber reinf 30% Filler by weight Carbon fiber reinforced m
- Application Areas:Electronic and electrical Microswitch
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:24hr | ASTMD955 | 0.10到0.40 | % |
| TD:24hr | ASTMD955 | 0.70到1.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | --2 | ASTMD638 | 30300 | Mpa |
| -- | ISO527-2/1 | 28600 | Mpa | |
| Tensile strength | Yield3 | ASTMD638 | 157 | Mpa |
| Yield | ISO527-2/5 | 133 | Mpa | |
| Break3 | ASTMD638 | 157 | Mpa | |
| Break | ISO527-2/5 | 133 | Mpa | |
| elongation | Yield3 | ASTMD638 | 0.74 | % |
| Yield | ISO527-2/5 | 0.56 | % | |
| Break3 | ASTMD638 | 0.74 | % | |
| Break | ISO527-2/5 | 0.56 | % | |
| Bending modulus | 50.0mmSpan4 | ASTMD790 | 19100 | Mpa |
| --5 | ISO178 | 20600 | Mpa | |
| Bending stress | --5,6 | ISO178 | 46.0 | Mpa |
| Yield,50.0mmSpan4 | ASTMD790 | 206 | Mpa | |
| Break,50.0mmSpan4 | ASTMD790 | 206 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 280 | °C |
| 0.45MPa,Unannealed,64.0mmSpan8 | ISO75-2/Bf | 281 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 267 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan8 | ISO75-2/Af | 268 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 1E-06 | cm/cm/°C |
| MD:23to60°C | ISO11359-2 | 1E-06 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 4.6E-06 | cm/cm/°C | |
| TD:23to60°C | ISO11359-2 | 4.6E-06 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 260 | J/m |
| 23°C7 | ISO180/1U | 14 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.